- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 228 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 228 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYblend 45FS GKF2010 PC/ABS-Blend, Glass Fiber reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C @Thickness 3.20 mm |
228 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Cycoloy® C6800 PC+ABS (Asia Pacific) PC+ABS, nonchlorinated, nonbrominated flame retardant.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPC 05ENH Polypropylene Copolymer, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C @Thickness 3.20 mm |
228 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Cycoloy® C6800 PC+ABS PC+ABS, nonchlorinated, nonbrominated flame retardant.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Halar® 1400LC Polyethylene, Chlorotrifluoroethylene (ECTFE)
(Unverified Data**) Information provided by Solvay Specialty Polymers. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | Unannealed; ASTM D648 |
| Phillips 66 COPYLENE® CR030LN Polypropylene, Mini-Random Copolymer, Thermoforming COPYLENE™ CR030LN is a mini-random copolymer with a high performance nucleation system designed to yield high clarity thermoformed articles.Applications: ThermoformingInformation provided by Philli.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Flint Hills P4C5B-030 Homopolymer Polypropylene Homopolymer, UL certified, and FDA compliant.Features: Nucleated, antistat, and controlled rheology.Applications: Injection molding: closures and excellent mold release.Former Huntsman polypropylene.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 1-3610 UW Polypropylene Homopolymer INNOPOL® CS 1-3610 UW is a white colored, flame retarded and UV-stabilized polypropylene homopolymer compound.INNOPOL® CS 1-3610 UW is recommended for producing electric articles by injection .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 2-9000 MA N Polypropylene Copolymer INNOPOL® CS 2-9000 MA N is a high melt flow copolymer with antistatic additive.INNOPOL® CS 2-9000 MA N is developed for producing injection molded automotive components.All information provide.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| LyondellBasell Astryn 65F4-2 Polypropylene Homopolymer, 20% Talc Key Features: conventional melt flow, high modulus, mineral-filled polypropylene homopolymer, excellent impact and stiffness balance, good dimensional stability, excellent heat resistance, good colo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Flint Hills P6C6B-134 General Purpose Impact Copolymer Polypropylene Features: Good processability, nucleated with Antistat. Product does not contain animal derived components.Applications: Injection molding - lawn and garden partsInformation provided by Flint Hill.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ISO Method 180 |
| LyondellBasell Astryn BB77G Polypropylene Copolymer, 15% Talc Key Features: high melt flow, high modulus, UV-stabilized, mineral-filled polypropylene copolymer, good impact stiffness and balance, good dimensional stability, good colorability, good aesthetics, .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 9710 PP SABIC® PPcompound 9710 is a mineral filled, impact modified polypropylene TPO. This material combines high impact resistance, scratch resistance, and heat stability with interior automotive UV st.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C @Thickness 3.20 mm |
228 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON MD000AP PP LNP* STAT-KON* MD000AP is a compound based on Polypropylene containing Carbon Powder. Added features of this grade include: Electrically Conductive, Exceptional Processing. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Xenoy® 1105 PBT+PC (Asia Pacific) PBT/PC blend, injection molding grade, non-reinforced, impact modified, excellent toughness at low temperatures, very good paintability |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | Unannealed; ASTM D648 |
| Styron EMERGEâ„¢ 9500CR Polycarbonate (PC) / Polyethylene Terephthalate (PET) Overview: EMERGEâ„¢ PC/PET 9500 CR advanced resin is a polycarbonate blend with excellent chemical resistance and ignition resistance properties. This grade was designed for use in medical equipm.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM Test |
| Styrolution Terblend® N NG-02 8% Glass Filled ABS/PA6 (Dry) Terblend N NG-02 is a glass fibre reinforced ABS/PA6 blend with excellent dimensional stability, high impact strength and good surface appearance.Information provided by STYROLUTION, which is a join.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Eastman Tritan EX401 Copolyester Eastman Tritan EX401 is an amorphous copolyester with excellent appearance and clarity. Tritan EX401 contains a mold release derived from vegetable based sources. Its most outstanding features are.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Eastman Tritan LX201 Copolyester Eastman Tritan LX201 is an amorphous copolyester with excellent appearance and clarity. Tritan LX201 contains a mold release derived from vegetable based sources. Its most outstanding features are.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Eastman Tritan MX810 Copolyester Applications:Blood TherapyDialyzer HousingsIV ComponentsKey Attributes:Ease of processingExcellent clarityExcellent hydrolytic stabilityFast drying timesGood chemical resistanceOutstanding impact re.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Eastman Tritan MX811 Copolyester Applications:Blood TherapyDialyzer HousingsIV ComponentsKey Attributes:Ease of processingExcellent clarityExcellent hydrolytic stabilityFast drying timesGood chemical resistanceGood heat resistanceO.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Eastman Tritan TX2000 Copolyester Eastman Tritan TX2000 is an amorphous copolyester with excellent appearance and clarity. Its most outstanding features are excellent toughness, hydrolytic stability, and heat and chemical resistanc.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Aclo Accutech ABS ABS892EV High Heat Grade Approved to GM7001M |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Carmel Olefins CAPILENE® T 12 EV Polypropylene Homopolymer CAPILENE® T 12 EV is a polypropylene homopolymer with narrow molecular weight distribution, controlled rheology, intended for fiber applications. It is characterized by easy processing, very good m.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Aclo Accutech Polypropylene Copolymer CP0436T30L Talc Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Cheng Yu Plastic A703G2 ABS 20% Glass Fiber Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ISO 75-1/-2 |
| Covestro Makroblend® DP 6015 Polycarbonate + PBT Developmental product(PC+PBT)-blendimpact modifiedeasy releaseinjection molding grade. Makroblend DP 6015* provides an outstanding balance of low-temperature impact strength and excellent chemical .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Xenoy® XD1647 PBT+PC (Europe-Africa-Middle East) XENOY XD1647 is a semi crystalline, impact modified PBT+PC blend, containing 15% mineral filler. It is especially developed to obtain a reduced coefficient of thermal expansion combined with good ch.. |
|||