| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
| Braskem HB 0055 HDPE Blow Molding Polyethylene
(discontinued **) Applications: 200 liters L-ring drums. Information provided by Braskem |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
| Braskem BT 100K HDPE Blow Molding Polyethylene
(discontinued **) Applications: Large containers from 60 to 200 litersInformation provided by Braskem |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
| Braskem BT 003 HDPE Blow Molding Polyethylene
(discontinued **) Applications: Bottles for food products, lubricating and cooking oil; toys; bottler for surface-active agents; sheets. Information provided by Braskem |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
| LyondellBasell Alathon® M5363 High Density Polyethylene ApplicationsALATHON L 4912 is a high molecular weight, high density copolymer with a broad molecular weight distribution. This resin provides excellent stiffness and a good balance of film properti.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
| LyondellBasell Alathon® M5370 High Density Polyethylene ApplicationsALATHON M 5370 copolymer with narrow weight distribution. This resin provides high impact strength and stress crack resistance, excellent color, low odor and good processability. Typic.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | ASTM D648 |
| Ineos R01C-00 Polypropylene Random Copolymer Grade R01C-00 is a low flow rate, high clarity random copolymer designed for extrusion, thermoforming and blow molding, through it is clarifier/antistat additive combination. Applications that requi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® HDPE 8904 UV GY Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Good UV ResistanceAppearance: GreyInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | Annealed; ASTM D648 |
| Spartech Royalite R60M Hi-Impact ABS/PVC Resin Data provided by the manufacturer. This rigid, fire-rated, proprietary resin is specifically formulated to meet the requirements of the FAR 25.853 A flammability test. Primary applications are air.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | ASTM D648 |
| Spartech Solarex® SV Copolyester Sheet Description: Copolyester SheetInformation provided by Spartech. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | unannealed (0.125 in); ASTM D648 |
| Styron EMERGEâ„¢ 5710 Acrylonitrile Butadiene Styrene (ABS) EMERGEâ„¢ ABS 5710 advanced resin is an ignition resistant ABS resin with an excellent balance of flow and impact strength. Applications: Monitor Enclosures Surge Protectors and UPS Enclosures .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
| Borealis Borecene™ RM7402 Linear Polyethylene for Rotational Molding Borecene RM7402 is a third generation linear medium density natural polyethylene for rotational molding. The narrow molecular weight distribution imparted through metallocene catalyst technology pro.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ISO 75-2 |
| Borealis Borpact™ SG910MO Polypropylene for Injection Molding Borpact™ SG910MO is a high impact and transparent polypropylene. This grade provides high gloss, high transparency and excellent impact properties. Applications: containers and products with medium.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ISO 75-2 |
| Borealis BorPURE™ RE450MO Polypropylene Random Copolymer BorPure™ RE450MO is a specially modified highly-transparent polypropylene random copolymer with medium melt flow rate. This grade is characterized by optimum combination of high impact strength and.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C @Thickness 3.20 mm |
162 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 389 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | ASTM D648 |
| A. Schulman LB502-01 High Molecular Weight, High-Density Polyethylene Copolymer DescriptionLP 502-01 Natural is a high molecular weight, high-density polyethylene copolymer, designed for blow molding of large parts where the finished product demands outstanding physical perform.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | ASTM D648 |
| A. Schulman LB502-01 High Molecular Weight, High-Density Polyethylene Copolymer DescriptionLP 502-01 Natural is a high molecular weight, high-density polyethylene copolymer, designed for blow molding of large parts where the finished product demands outstanding physical perform.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C @Thickness 3.20 mm |
162 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 389 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | ASTM D648 |
| A. Schulman LB502-01 High Molecular Weight, High-Density Polyethylene Copolymer DescriptionLP 502-01 Natural is a high molecular weight, high-density polyethylene copolymer, designed for blow molding of large parts where the finished product demands outstanding physical perform.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ISO 75-2 |
| Borealis Daplen™ SB4411/2 Polypropylene Compound Elastomer and Mineral Modified Daplen SB4411/2 is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. The product is available in black, but other colors can be provided on request.Daplen .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
| Eastman Tenite 285A2R30020 Cellulose Acetate Butyrate, Natural, Trsp Applications:Tool handlesToys/sporting goodsProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clar.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
| Eastman TiGlaze SV Copolyester TiGLAZE SV copolyester is a specialty copolyester for the architectural glazing industry, designed to provide a unique balance of toughness, stiffness and material value. The material has a CC1 Ligh.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | ASTM D648 |
| ExxonMobil PP9513 Polypropylene Homopolymer Product Description: A random copolymer resin designed for non-oriented film.Availability: North America Features:Controlled RheologyEthylene Oxide SterilizableUses: BagsCast FilmHeavy-duty BagsPac.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | Unannealed; ASTM D648 |
| Dow R792-35RNA Polypropylene Random Copolymer Resin OverviewControlled rheology productConsistent processabilityContains clarifying additiveContains an antistatic additiveComplies with U.S. FDA 21 CFR 177.1520 (c)3.1a, Canadian HPFB No ObjectionDOW R.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM-D648 |
| Braskem AC59 HDPE Monofilament Polyethylene Homopolymer AC59 resin is a high-density polyethylene homopolymer produced by the solution process and designed for monofilament applications. It contains antioxidant additives. Its applications include: film .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM-D648 |
| Braskem GP100OR HDPE High Density Extrusion Polyethylene GP100OR is a high-density polyethylene compound specially developed for the manufacturing of extruded pipes for gas distribution. It is produced with bimodal technology and has high molar mass. It s.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | ASTM D648 |
| Aclo Accutech Polypropylene Copolymer CP0437C10L Calcium Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | |
| BASF Novolen® 2309 L Polypropylene Cast film and thermoformed partsData was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | unannealed; ASTM D-648 |
| Axiall 8607 Rigid PVC, Extrusion Georgia Gulf 8607 is a special purpose pelletized compound formulated for high impact, rigid extrusion profiles.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ISO 75 |
| GEHR Plastics PVC-U Polyvinylchloride Polyvinyl chloride is a flame retardant material with an exceptional chemical resistance and also with lower stress cracking. PVC-U shows high mechanical strength, tensile strength and the continuou.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 - 133 °C | 162 - 271 °F | Average value: 91.9 °C Grade Count:58 |
| Overview of materials for Polypropylene, Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Blow Molding Grade". Each property range of values reported is minimum and maximum values.. |
|||