Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C @Thickness 3.20 mm |
147 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
Ovation Polymers Opnyl OP6MT254 Nylon 6 Nylon 6 – Mighty Tough plasticized extrusion grade for tubing/profile applications. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are p.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | ASTM D648 |
LyondellBasell Alathon® ETP H4745 High Density Polyethylene ApplicationsALATHON H 4745 is a new, multi-purpose, high-flow resin featuring enhanced cold temperature impact performance, enhanced processability and thermal stability for fast cycling and exhibit.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | ASTM D648 |
LyondellBasell Alathon® ETP H4837 High Density Polyethylene ApplicationsALATHON H 4837 is a high-flow “freezer†grade resin that exhibits enhanced cold temperature impact performance, enhanced processability and thermal stability, with good color a.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | ASTM D648 |
LyondellBasell Alathon® H4620 High Density Polyethylene, Injection Molding Grade Alathon H4620 is a medium-flow resin that exhibits good cold temperature impact performance, enhanced processing and thermal stability. Typical applications are thinner-walled parts that require che.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | ASTM D648 |
LyondellBasell Alathon® M4855 High Density Polyethylene, Injection Molding Grade ALATHON M4855 is a high density copolymer for use in injection molding applications. It exhibits excellent impact, warp and environmental stress crack resistance. Typical applications for M4855X01 a.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | molding; ASTM D648 |
LyondellBasell Petrothene® LP540200 High Density Polyethylene, Film Extrusion Grade PETROTHENE LP540200 is a copolymer resin designed for blown film applications. This resin offers high ESCR, stiffness, excellent appearance and bubble stability. LP540200 is recommended for high str.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | Molded; ASTM D648 |
LyondellBasell Petrothene® LP540200 High Density Polyethylene ApplicationsPETROTHENE LP 5402-00 is a copolymer resin designed for blown film applications. This resin offers high stiffness, excellent appearance and bubble stability and good draw-down. LP 5402-0.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.9 °C | 147 °F | Unannealed; ISO 75B-1, -2 |
LyondellBasell Hifaxâ„¢ ETA3081HS Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ ETA3081HS medium melt flow, 800 MPa flexural modulus, paintable thermoplastic elastomeric olefin (TEO) resin has balanced physical properties, moldability and paintability. .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.9 °C | 147 °F | Unannealed; ISO 75B-1, -2 |
LyondellBasell Hifaxâ„¢ RTA3263EUV/1 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ RTA3263EUV/1 fractional melt flow, 1,700 MPa flexural modulus, UV-stabilized, mineral-filled, extrusion grade thermoplastic elastomeric olefin (TEO) resin has an excellent b.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | ISO 75-2 |
Borealis Borcom™ WG140AI Polypropylene Borcom™ WG140AI is a polypropylene microcomposite intended for injection molding. This material has an excellent balance between impact strength and stiffness, high melt flow rate and gives a good.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C @Thickness 3.20 mm |
147 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C @Thickness 3.20 mm |
147 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C @Thickness 3.20 mm |
147 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C @Thickness 3.20 mm |
147 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C @Thickness 3.20 mm |
147 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C @Thickness 3.20 mm |
147 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | Method A; ASTM D-648 |
Chevron Phillips Marlex® HMN TR-942/942G Polyethylene; HDPE High density polyethylene. These hexene copolymers are tailored for rotational molding applications that require: Wide process windows and fair flowLong-term UV stabilizationExcellent impact stren.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | Method A; ASTM D-648 |
Chevron Phillips Marlex® HMN TR-945/945G Polyethylene; HDPE High density polyethylene. These hexene copolymers are tailored for rotational molding applications that require: Wide process windows and excellent flowLong-term UV stabilizationGood impact stren.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 63.9 °C | 147 °F | ISO 75-2/B |
ExxonMobil HDPE HMA 018 High Density Polyethylene Resin Product Description: HMA 018 is an easy flow HDPE grade, characterized by high gloss and dimensional stability. Availability: Africa & Middle East, Asia Pacific and Europe Additive: Thermal Stabili.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | |
Arkema Group Rilsan® MB 3750 Nylon 11, Transparent Grade (Dry) Designation ISO 1874-PA11/xx,F,THL,22-020Transparent semi-crystalline PA11 grade.Used for film extrusion and injection molding (low thickness).Very good low temperature impact strength.High chemical.. |