Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 - 199 °C | 124 - 390 °F | Average value: 146 °C Grade Count:9 |
Overview of materials for Thermoplastic Polyurethane, Elastomer, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane, Elastomer, Glass Filled". Each property range of values reported is minimum .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ISO 75/Method Bf |
Premix Thermoplastics PRE-ELEC® PE 1313
(discontinued **) PRE-ELEC PE 1313 is a conductive thermoplastic compound based on PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PE 13.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.2 °C | 124 °F | ASTM D648-98c |
DSM Somos® WaterClear® 10110 Epoxy Resin for Stereolithography
(discontinued **) DescriptionDSM Somos® 10110 is a high-speed liquid photopolymer that produces strong, rigid, and durable parts with optical clarity using stereolithography machines. This material is especially us.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C @Thickness 3.20 mm |
124 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP LUBRICOMP TX97446 PU LNP* LUBRICOMP* TX97446 is a compound based on Polyurethane containing Proprietary Fillers. Added feature of this material is: Wear Resistant. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene DescriptionPolyfort® PP 3702 is a clarified copolymer polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene DescriptionPolyfort® PP 3702 is a clarified copolymer polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene DescriptionPolyfort® PP 3702 is a clarified copolymer polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene DescriptionPolyfort® PP 3702 is a clarified copolymer polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene DescriptionPolyfort® PP 3702 is a clarified copolymer polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene DescriptionPolyfort® PP 3702 is a clarified copolymer polypropylene.Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ISO 75 |
Unitika TERRAMAC TE-1030 Polylactic Acid (PLA) High-Impact grade, Injection grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ASTM D648 |
Lubrizol ESTALOC® 59010 Polyester-Type, Reinforced Engineering Thermoplastic Polyurethane Features: Fast Cycling, Dimensional Stability, Durability, Aesthetics, Low Temperature ImpactUses: Injection MoldingAvailability: Americas and AsiaInformation provided by Lubrizol |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ASTM D648 |
Lubrizol Estaloc® 59020 Reinforced Thermoplastic Polyurethane Type: Estaloc® 59020 RETPU is a polyester-type reinforced engineered thermoplastic polyurethane (RETPU).Features: Fast cycling, dimensional stability, durability, aesthetics, low temperature impact.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ASTM D648 |
Chevron Phillips Marlex® 7104 LLDPE Sheet Extrusion Resin Type: Hexene CopolymerCharacteristics: Outstanding ESCRGood melt strengthExcellent flexibilityGood processabilityGood glossHigh COFApplications: Landfill coversFlat and round-die productsCoext.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | Method A; ASTM D648 |
Chevron Phillips Marlex® K203 LLDPE Sheet Extrusion Resin Type: Hexene CopolymerCharacteristics: Outstanding ESCRBroad fusion rangeExcellent melt strengthGood processabilityExcellent flexibilityImproved output and texturingApplications: Coextruded ca.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.1 °C | 124 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
Dow DNDA-1081 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-1081 NT 7 is produced using UNIPOL™ PE process technology. It is intended for high-speed injection molding of thin walled parts such as downguaged lids. Information provided by Dow |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.1 °C | 124 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
Dow DNDA-1149 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-1149 NT 7 is produced using UNIPOL™ PE process technology and is intended for high-speed injection molding applications. Information provided by Dow |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.1 °C | 124 °F | ASTM D648 |
Aclo Accutech Polypropylene Copolymer CP0436C10L1 Calcium Reinforced |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ASTM-D648 |
Braskem Symbios 3102 Polypropylene Terpolymer Braskem Symbios 3102 is a medium melt flow rate terpolymer with a heat seal temperature below 110ºC on its non-treated face. It is designed for use as a heat sealing layer for cast film coextrusion.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 - 54.0 °C | 124 - 129 °F | ASTM D648 |
3D Systems Accura® 40 Plastic for SLA® Systems 40 Accura "Nd" type material - for use with Viper SLA, and SLA 3500, 5000 and 7000 systems.ApplicationsHigh temperature testing:Automotive "under-the-hood" partsIntake manifoldsLighting components a.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ASTM D648 |
Ashley Polymers Ashlene® 847 Nylon 6, Film Grade A very high impact, low flexural modulus Nylon 6 resin for molding or extrusion. Outstanding low temperature properties.Data provided by the manufacturer |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.0 - 161 °C | 124 - 322 °F | Average value: 136 °C Grade Count:12 |
Overview of materials for Nylon 6, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Film Grade". Each property range of values reported is minimum and maximum values of appropriat.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 51.1 - 135 °C | 124 - 275 °F | Average value: 91.2 °C Grade Count:32 |
Overview of materials for Polypropylene with 10% Calcium Carbonate (CaCO3) Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 10% Calcium Carbonate (CaCO3) Filler". Specific grades with primary filler content be.. |