- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 87.8 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 87.8 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| RheTech Products FT7016-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Bumper coversCladdingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| RheTech Products FT7016-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Bumper coversCladdingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| RheTech Products P252-00 Polypropylene Copolymer, Natural Applications: Interior trimUnderhood componentsElectrical housingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| RheTech Products P252-670UV Polypropylene Copolymer, UV Stabilized, 134B Stone Applications: Interior trimElectrical housingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Polymer Resources ABS-FR Flame Retardant ABS Flame Retardant Acrylonitrile Butadiene StyreneFeatures: • Flame Retardant • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Polymer Resources ABS-FR-[color]-UV Flame Retardant ABS, UV-stabilized Flame Retardant Acrylonitrile Butadiene Styrene, UV-stabilizedFeatures: • Flame Retardant • Self Extinguishing • Good UV ResistanceProcess: Injection MoldingNotes: All physical, mechanical and.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Polymer Resources ABS-GP1-[color]-3 ABS, General Purpose, UV-stabilized Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Polymer Resources ABS-GP-IM General Purpose ABS, Impact Modified General Purpose Acrylonitrile Butadiene Styrene, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Polymer Resources PPX-FR1-[color]-EN Modified-PPO, V-0 Flame Retardant, Extrusion Grade Modified-Polyphenylene Oxide, V-0 Flame Retardant, 190F HDT, Extrusion GradeFeatures: • Bromine Free • Chlorine FreeProcess: ExtrusionNotes: All physical, mechanical and thermal testing conducte.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Polymer Resources PPX-MF-FR1 Modified-PPO, V-0 Flame Retardant, Mineral Reinforced Modified-Polyphenylene Oxide, V-0 Flame Retardant, 190F HDT, Mineral ReinforcedFeatures: • Bromine Free • Chlorine Free • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mecha.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 - 190 °C | 190 - 374 °F | Average value: 133 °C Grade Count:41 |
| Overview of materials for Polyphenylene Ether, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Molded". Each property range of values reported is minimum and maximum values of ap.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | Unannealed; ISO 75B-1, -2 |
| LyondellBasell Pro-faxâ„¢ SG899 Polypropylene Copolymer Description: Pro-faxâ„¢ SG899 high flow, high impact polypropylene copolymer resin is tailored for use in automotive interior head impact applications. This resin is designed to be run in convent.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Ineos R35C-00 Polypropylene Random Copolymer Grade R35C-00 is a high clarity random copolymer with a high flow rate. This material is designed for high speed injection molding and meets the requirements of the U.S. Food and Drug Administration.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Ineos R35C-01 Polypropylene Random Copolymer Grade R35C-01 is a high clarity random copolymer with a high flow rate. This material is designed for high speed injection molding and meets the requirements of the U.S. Food and Drug Administration.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Ineos L24G-00 Polypropylene Impact Copolymer Grade L24G-00 is a high melt flow rate, antistatic high impact copolymer polypropylene for injection molding applications. It offers excellent impact resistance and a high flexural modulus. This mat.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Spartech PE4312 Reinforced High Density Polyethylene Compound Spartech Polycom's filled high molecular weight, high density polyethylenes are specifically designed for blow molding and sheet extrusion /thermoforming of structural parts. These materials offer a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Spartech Royalite R59 ABS/PVC Fire Rated Sheet Description: Fire Rated SheetInformation provided by Spartech. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| A. Schulman PP 828S-01 Polypropylene Medium Impact Molding Grade Polypropylene DescriptionPolypropylene PP 828S-01 is a medium impact molding grade created for applications needing good impact and higher H.D.T., such as tote bins, automotive ducting and housings. Information p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| A. Schulman PP 828S-01 Polypropylene Medium Impact Molding Grade Polypropylene DescriptionPolypropylene PP 828S-01 is a medium impact molding grade created for applications needing good impact and higher H.D.T., such as tote bins, automotive ducting and housings. Information p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ISO 75 |
| A. Schulman SCHULAMID® 6 MV14 Unreinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ISO 75 |
| A. Schulman SCHULAMID® 6 MV14 Unreinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ISO 75-2/B |
| ExxonMobil PP7054L1 Polypropylene Impact Copolymer Product Description: A nucleated impact copolymer resin with medium flow. It is suitable for molding applications like consumer products, closures, containers, toys and rigid packaging applications.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | Unannealed; ASTM D648 |
| Dow C133-02 Polypropylene Impact Copolymer Resin OverviewDow C133-02 Polypropylene Resin is intended for use in extrusion, thermoforming, and extrusion blow molding applications where impact at refrigeration temperatures is desired. It is especia.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Aclo Accutech Polypropylene Copolymer CP0437T20L Talc Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Amco PRIMATOP PP CO 005NB Fractional Melt Polypropylene Copolymer Features:heat aging resistanceimpact resistancelow temperature melt strengthgood stiffnessApplications:containerspipestoysextrusion coatingFormer A-Top Polymers product; part of Amco product line si.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Americas Styrenics STYRON A-TECH® 1400AS High Impact Polystyrene Product CharacteristicsHigh FlowGood ImpactFood Contact CompliantTypical ApplicationsTelevision housingsPrinter HousingsConsumer goodsInformation provided by AmericasStyrenics LLC. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Aclo Accuguard Polypropylene HP1369V2CSL Homopolymer Flame Retardant Copper Stabilized |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Aclo Accutech Polypropylene Copolymer CP0436T10L Talc Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Asahi Kasei Thermofil P-9900-0576 Unreinforced, Flame Retardant, Heat Stabilized Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Polymer Resources PPX-FR1 Modified PPO, UL 94 V-0 with HDT of 190 F
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||