Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C @Thickness 3.18 mm |
129 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Maxxam™ FR PE 152 Polyethylene, Unspecified (PE, Unspecified) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ASTM D648 |
Formosa Plastics Formolene® L63935 Rotational Molding LLDPE
(discontinued **) Hexene CopolymerApplications: Tanks, toys and other non-tank rotational molding applicationsMeets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ASTM D648 |
Formosa Plastics Formolene® L63935U Rotational Molding LLDPE
(discontinued **) Hexene CopolymerApplications: Tanks, toys and other non-tank rotational molding applicationsFormolene L63935U is fully heat and UV stabilized.Meets all requirements of the U.S. Food and Drug Adminis.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 - 144 °C | 129 - 291 °F | Average value: 119 °C Grade Count:97 |
Overview of materials for Polypropylene with 30% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Talc Filler". Specific grades with primary filler content between 25% and 34% are.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ASTM D648 |
DSM Somos® 8110 Epoxy Photopolymer
(discontinued **) DescriptionDSM Somos® 8110 is a high-speed liquid photopolymer that produces flexible, high-impact-strength, accurate parts using stereolithography machines. It has a wide processing latitude and .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ASTM D648 |
DSM Somos® 8120 Epoxy Photopolymer
(discontinued **) DescriptionDSM Somos® 8120 is a high-speed liquid photopolymer that produces flexible, high-impact-strength, accurate parts using stereolithography machines. It has a wide processing latitude and .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ISO 75-1/-2 |
Lanxess Durethan® CI 31 F 000000 Copolyamide PA6/6I Copolyamide PA6/6I, low melt point (188-191°C), low viscosity, no additives, very high transparency, in compliance with FDA as far as the PA-layer is separated from the food by a 50 µm PE film.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ISO 75-2 |
Borealis Bormed™ LE6609-PH LDPE for Pharmaceutical Blow Molding Bormed LE6609-PH is a LD-polyethylene produced in a high-pressure process intended for blow molding of soft and flexible packages for pharmaceutical products.Bormed LE6609-PH can be used in "blow-fi.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ISO 75 |
Unitika TERRAMAC TE-1070 Polylactic Acid (PLA) High-Impact grade, Injection grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ASTM D648 |
Buckeye Polymers BP RPP 2508 T Polypropylene, 25% Mineral Filled This Talc-filled product exhibits excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and mar resistance, and resis.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 - 77.0 °C | 129 - 171 °F | ASTM D648 |
Arkema Group KYNAR FLEX® 3120-15 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Flexible, flame and smoke suppressant. High stability in harsh thermal, chemical and ultraviolet environments. High toughness.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 - 77.0 °C | 129 - 171 °F | ASTM D648 |
Arkema Group KYNAR FLEX® 3120-50 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Flexible, 150°C temperature rating. High stability in harsh thermal, chemical and ultraviolet environments. High toughness a.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | 90 Minute UV Cure; ASTM D648 |
3D Systems Accura® SI 40 Plastic for the SLA® 500 System Accura 40 "Ar" or "Hc" type materials - for the SLA 500 system. Mimics Nylon 6:6ApplicationsHigh temperature testing:Under hood bolt-on testingWind tunnel testingHVAC testingPrototyping and testing .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ASTM D648 |
ExxonMobil Escorene® HD-8660 HDPE, Rotational Molding Pellets
(discontinued **) Data Provided by Exxon Chemical Canada.Characteristics: Fully formulated UV-8 type protection, Higher stiffness & impact strengthUses: Large agricultural tanks, Industrial products |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ASTM D648 |
ExxonMobil Escorene® HD-8661 HDPE, Rotational Molding Powder
(discontinued **) Data Provided by Exxon Chemical Canada.Characteristics: Fully formulated UV-8 type protection, Higher stiffness & impact strengthUses: Large agricultural tanks, Industrial products |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C @Thickness 3.20 mm |
129 °F @Thickness 0.126 in |
ISO 75 |
A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | CP-TM-12 |
PolyOne Elastamax HTE 2101-1002 Polyurethane Alloy
(discontinued **) This is an extrusion grade polyurethane alloy. Physical Form: Pellet. Standard Color: Off white, opaque.Information provided by M. A. Hanna. M. A. Hanna and Geon merged to form PolyOne in 2000. .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | Rate B; ASTM D648 |
Samyang Triel® 5300 Thermoplastic Polyether Ester Elastomer TRIEL® resins offer superior mechanical properties, elasticities, heat and chemical resistance, which allow it to be widely used for electric/electronic equipments, automotive parts and outdoor rec.. |