Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 °C @Thickness 3.18 mm |
104 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Maxxam™ FR MF5420-0085 NHFR Polypropylene, Unspecified (PP, Unspecified) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 - 45.0 °C | 104 - 113 °F | ASTM D648-06 |
Proto3000 Objet Digital Materials™ DM_4310 Polypropylene-like Prototyping Polymer Primary material: DurusWhiteSecondary material: VeroWhitePlus, VeroBlue, VeroBlack or FullCure720Digital Materials are made up of two Objet materials. The two materials are combined in specific conc.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 - 45.0 °C | 104 - 113 °F | ASTM D648-06 |
Proto3000 Objet Digital Materials™ DM_4410 Polypropylene-like Prototyping Polymer Primary material: DurusWhiteSecondary material: VeroWhitePlus, VeroBlue, VeroBlack or FullCure720Digital Materials are made up of two Objet materials. The two materials are combined in specific conc.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 - 45.0 °C | 104 - 113 °F | ASTM D648-06 |
Proto3000 Objet Digital Materials™ DM_4510 Polypropylene-like Prototyping Polymer Primary material: DurusWhiteSecondary material: VeroWhitePlus, VeroBlue, VeroBlack or FullCure720Digital Materials are made up of two Objet materials. The two materials are combined in specific conc.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 - 45.0 °C | 104 - 113 °F | ASTM D648-06 |
Proto3000 Objet Digital Materials™ DM_4710 Polypropylene-like Prototyping Polymer Primary material: DurusWhiteSecondary material: VeroWhitePlus, VeroBlue, VeroBlack or FullCure720Digital Materials are made up of two Objet materials. The two materials are combined in specific conc.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 - 43.0 °C | 104 - 109 °F | ASTM D648-06 |
Proto3000 Objet Digital Materials™ DM_8425 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 - 45.0 °C | 104 - 113 °F | ASTM D648-06 |
Proto3000 Objet Digital Materials™ DM_8505Gray20 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 - 45.0 °C | 104 - 113 °F | ASTM D648-06 |
Proto3000 Objet Digital Materials™ DM_8505Gray25 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 - 45.0 °C | 104 - 113 °F | ASTM D648-06 |
Proto3000 Objet Digital Materials™ DM_8505Gray35 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 - 45.0 °C | 104 - 113 °F | ASTM D648-06 |
Proto3000 Objet Digital Materials™ DM_8505Gray40 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 - 43.0 °C | 104 - 109 °F | ASTM D648-06 |
Proto3000 Objet Digital Materials™ DM_8505Gray50 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 °C | 104 °F | ASTM D648 |
DuPont™ Surlyn® 9970 Ionomer Resin, Zinc
(discontinued **) Surlyn® 9970 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 °C | 104 °F | ASTM D648 |
LyondellBasell Petrothene® NA814000 Low Density Polyethylene ApplicationsPETROTHENE NA 814-000 is a low density homopolymer resin specifically developed for a wide variety of blow molding applications. This resin exhibits excellent gloss, an excellent balanc.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 °C | 104 °F | ASTM D648 |
LyondellBasell Petrothene® NA831000 Low Density Polyethylene ApplicationsPETROTHENE NA831-000 resin exhibits high stress crack resistance and low temperature brittleness. Typical applications include housewares, containers and industrial parts. Regulatory St.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 °C | 104 °F | ASTM D648 |
DuPont™ Surlyn® 8020 Ionomer Resin, Sodium Surlyn® 8020 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neu.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 °C | 104 °F | ASTM D648 |
DuPont™ Surlyn® 9020 Ionomer Resin, Zinc Surlyn® 9020 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The resin contains an addit.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 °C | 104 °F | Compression molded; ASTM D648 |
Dow 620I Linear Low Density Polyethylene (LDPE) For extruded foam applications Complies with U.S. FDA 21 CFR 177.1520 (c) 2.1 Information provided by Dow |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 - 72.8 °C | 104 - 163 °F | Average value: 44.7 °C Grade Count:18 |
Overview of materials for Low Density Polyethylene (LDPE), Molded This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Molded". Each property range of values reported is minimum and maximum .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 - 54.0 °C | 104 - 129 °F | Average value: 47.0 °C Grade Count:7 |
Overview of materials for Low Density Polyethylene (LDPE), Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Blow Molding Grade". Each property range of values reported is minimum .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 40.0 °C | 104 °F | ASTM D648 |
DuPont™ Surlyn® 9730 Ionomer Resin, Zinc
(discontinued **) Surlyn® 9730 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr.. |