- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 232 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 232 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C @Thickness 6.35 mm |
450 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| PolyOne LubriOne™ NN-000/10T Polyamide 66 (Nylon 66) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | ASTM D648 |
| Nilit Polynil® P230 High Viscosity Nylon 66 Description: Polynil P230 is a high viscosity NYLON 66 (Viscosity number 280 cm³/gr) that was developed for film- and rod extrusion. It has high melt stability and low gel content. It holds various.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | ASTM D648 |
| Nilit Polynil® P240 High Viscosity Nylon 66 Description: Polynil P240 is a high viscosity NYLON 66 (Viscosity number 290 cm³/gr) that was developed for rod and slab extrusion. It has a high melt stability and a low gel content.Key characteri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | 0.125 in; ASTM D648 |
| Matrixx Group 84S7301 Flame Retardant 30% Glass Reinforced PET (V0)
(discontinued **) Data provided by The Matrixx Group, formerly RePlas. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 - 255 °C | 450 - 491 °F | Average value: 241 °C Grade Count:19 |
| Overview of materials for Nylon 66, Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Aramid Fiber Filled". Each property range of values reported is minimum and maximum values of .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP RN001 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RN001 is a compound based on Nylon 66 resin containing MOS2. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PA6/6 GB30 FR 30% Glass Bead Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 30% Filler by WeightAdditive: LubricantFeatures: Flame Retardant and LubricatedInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GB10 L 10% Glass Bead Filler Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 10% Filler by WeightAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GB15 15% Glass Bead Filler Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 15% Filler by WeightAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GB20 L BK 20% Glass Bead Filler Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 20% Filler by WeightAdditive: LubricantFeatures: LubricatedAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GB25 L BK 25% Glass Bead Filler Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 25% Filler by WeightAdditive: LubricantFeatures: LubricatedAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GB30 L 30% Glass Bead Filler Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 30% Filler by WeightAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6,6 GF33 HS L BK 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: LubricatedFeatures: LubricatedProcessing Method: Injection MoldingAppearance: .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 AF10 HS L Nylon 66 Availability: North AmericaForms: PelletsFiller/Reinforcement: Aramid Fiber, 10% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(10%)Features: Lubricated, Good Wear Resistance, Low Fric.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 AF10 Nylon 66 Availability: North AmericaForms: PelletsFiller/Reinforcement: Aramid Fiber, 10% Filler by WeightAdditive: LubricantFeatures: Lubricated, Good Wear Resistance and Low FrictionInformation provided by.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP 2F005 ETFE LNP* Thermocomp* 2F005 is a fluoropolymer compound based on ETFE containing 25% Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 WM40 IM HS 40% Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral Filler, 40% Filler by WeightAdditive: Heat Stabilizer and Impact ModifierFeatures: Heat Stabilized and Impact ModifiedProcessin.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | ASTM D648 |
| A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN100L (COND, 50% RH) Nylon 66, Internally Lubricated Information provided by Chase Plastics. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN100L (DAM) Nylon 66, Internally Lubricated Information provided by Chase Plastics. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN200L (DAM) Nylon 66, Internally Lubricated Information provided by Chase Plastics. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | ASTM D648 |
| A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | ASTM D648 |
| A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | ASTM D648 |
| Cheng Yu Plastic NG1100S Nylon 66, 10% Glass Fiber Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | ASTM D648 |
| A. Schulman ComAlloy Comtuf® 639 Nylon 6/6, Mineral Reinforced, Impact Modified, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company.40% Mineral reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | ASTM D648 |
| Asahi Kasei Thermofil N5-15FG-1103 15% Glass Fiber Reinforced, Lubricated Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 - 266 °C | 450 - 510 °F | Average value: 256 °C Grade Count:21 |
| Overview of materials for Nylon 66, Glass Fiber/MoS2 Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Fiber/MoS2 Filled". Each property range of values reported is minimum and maximum values.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 232 - 250 °C | 450 - 482 °F | Average value: 245 °C Grade Count:13 |
| Overview of materials for Polyethylene Terephthalate (PET), 40% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 40% Glass Reinforced". Specific grades with glass content between 35% .. |
|||