- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 218 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 218 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 425 °F | ASTM D648 |
| Polymer Resources NY66-MD02 Nylon, 2% Molybdenum disulfide for lubrication and wear (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ASTM D648 |
| Shell Carilon® DB6G6A10 Polyketone, 30% Glass-Reinforced General-Purpose Injection Molding Grade
(discontinue Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DB6G6A10 is a 30 percent short glass-fiber-reinforced, general purpose injection molding grade, wit.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ISO 75-1,-2 |
| Gromax BFG30-DN00N1 Nylon 6 30% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C @Thickness 3.20 mm |
424 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp JL003 PES LNP* Lubricomp* JL003 is a compound based on Polyethersulfone resin containing PTFE.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C @Thickness 3.20 mm |
424 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® ENH4565 PBT (Europe-Africa-Middle East) 33% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin, Good thermal shock resistance and low CTE. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 425 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6 GF35 HS L 35% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 35% Filler by WeightAdditive: Lubricant and Heat Stabilizer Features: Lubricated and Heat StabilizedProcessi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 425 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6 GF60 HS L 60% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 60% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedInformati.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 425 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6 GF40 ML2 HS UV BK 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 40% Filler by WeightAdditive: Heat Stabilized, Molybdenum Disulfide Lubricant and UV StabilizerFeatures: Lubricated, Good .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP JF004 PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004 is a compound based on Polyethersulfone resin containing Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 GF33 33% Glass Fiber Reinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 425 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 GF15H 30% Glass Fiber Reinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ASTM D648 |
| A. Schulman SCHULAMID® 6 GF33 33% Glass Fiber Reinforced Nylon 6 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ASTM D648 |
| A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® SK642FR NC010 Polybutylene Terephthalate (PBT) 15% Glass Reinforced Flame Retardant Polybutylene Terephthalate Crastin SK642FR is a 15% glass fibre reinforced flame retardant polybutylene terephthalate for injection moulding.It has a UL94 V-0 ra.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ASTM Test |
| BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Dry) Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 425 °F | Unannealed, 0.125 in bars; ASTM D648 |
| PolyOne Edgetek® NL-30CF/000 Nylon 6/12, Carbon Fiber Reinforced
(discontinued **) Description/Features:Carbon Fiber ReinforcedInformation provided by PolyOne Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | Unannealed; ASTM D648 |
| LNP Thermocomp® JF-1006 E LE BK8-055 Polyethersulfone, Glass Fiber Reinforcement
(discontinued **) Features: High Viscosity, Low ExtractablesForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many L.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C @Thickness 3.20 mm |
424 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® K4530 PBT 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors. |
|||