- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 175 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 175 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| Nylene® 204 (HS) , Fast Cycle Nylon 6 Description: Nylene® 204 (HS) is a fast cycle, medium viscosity, nucleated nylon 6. 204 is UL approved and automotive approved. Information provided by Custom Resins.ALM, Nylene Canada, and Custom .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| Nylene® 451 Nylon 6 Dry as molded. Injection molding grade. Nylene 451 is recommended for molding applications requiring both maximum durability and toughness. Exceptional fatigue and wear resistance insure long produ.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| Nylene® 600 Nylon 6 Dry as molded. Extrusion grade. Nylene 600 is a general purpose, medium viscosity, extrusion grade resin used in applications such as rods, slabs, and tubing. Other applications include wire jacke.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ISO 75, ASTM D648 |
| Nilit Nilamid B3 H ZA Unfilled, Low Temperature Impact Resistant PA6 Description: Nilamid B3 H ZA is a NYLON 6 with a low level of impact modification, allowing parts to be snap fitted in a dry-as-molded condition. It also has improved impact strength and elongation,.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| LATI Latamid SP1 PA 6.10 Polyamide 6.10 (PA6.10). Unfilled. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| LATI Latigray 75/4-01 CX/45 PBT Radiopaque compound based on Polybutylene Terephthalate (PBT). Special mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by L.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C @Thickness 3.20 mm |
347 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer LNP* LUBRICOMP* KCL34A is a compound based on Acetal Homopolymer resin containing 15% PTFE, 20% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C @Thickness 3.20 mm |
347 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp SX93441D PA6.12 LNP* Lubricomp* SX93441D is a compound based on Nylon 6/12 containing Proprietary Fillers. Characteristics of this grade are: Internally Lubricated.This data was supplied by SABIC-IP for the Ameri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D 648 |
| Shakespeare Isocorâ„¢ SVP6100 Nylon 610 Isocorâ„¢ 6100 is a medium viscosity PA-610. This resin is specifically suited for applications requiring low moisture absorption and greater dimensional stability. Isocorâ„¢ 6100 is also u.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D 648 |
| Shakespeare Isocorâ„¢ SVP6104 low viscosity PA-610 Isocorâ„¢ 6104 is a low viscosity PA-610. This resin is specifically suited for applications requiring low moisture absorption and greater dimensional stability. Isocorâ„¢ 6104 is also use.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Valox® VX3101N PBT (Europe-Africa-Middle East) VALOX VX3101N is an unreinforced PBT injection moulding resin, with excellent flow properties, good hydrolitical stability and chemical resistance. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP GX05482 PSU LNP* THERMOCOMP* GX05482 is a compound based on Polysulfone resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C @Thickness 3.20 mm |
347 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP GX05482 PSU LNP* THERMOCOMP* GX05482 is a compound based on Polysulfone resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® PA6/10 BK Nylon 610 Availability: North AmericaForms: PelletsAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL GTX GTX944 PPE+PA (Asia Pacific) NORYL GTX944 is an unfilled GTX grade with improved processability and increased impact performance. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL GTX GTX944 PPE+PA (Europe-Africa-Middle East) NORYL GTX944 is an unfilled GTX grade with improved processability and increased impact performance. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C @Thickness 3.20 mm |
347 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl GTX GTX6010 PPE+PA6 (Asia Pacific) PA6 based unfilled GTX. High impact.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| Tipco Tipcofil® AU 027 - Unfilled Nylon-6 Compound, with High Heat Stability, for Injection Molding Unreinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene DescriptionPolyflam® RPP 1133 is a 30% glass filled, flame retardant copolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene DescriptionPolyflam® RPP 1133 is a 30% glass filled, flame retardant copolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | dry; ISO 75-1/-2 |
| DSM Novamid® 1011CH5KR PA6 Heat Stabilized, Easy Molding Grade |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® BS PA6 Product description: Grilon BS is an unreinforced, heat stabilized standard PA6 injection molding grade with normal melt viscosity. Grilon BS has the following important properties: Good flow behavi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| Clariant Renol PA213 Nylon 6, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| E-Polymers TEKAMID® TB120L NCR , High Crystallinity PA6, DAM Precise injection, high crystallinityInformation provided by E-Polymers Co. Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| E-Polymers TEKAMID® TB120L Lubricated PA6, DAM LubricatedInformation provided by E-Polymers Co. Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| Arkema Group Rilsan® ASR 20 Nylon 12, 20% Carbon Fiber Filled (Conditioned) Designation ISO 1874-PA12,M,16-090,CF20Rigid grade with carbon fiber filler (20%) for injection molding. Available color: black. High strength-to-weight ratio. Very low shrinkage: include 0,5% on av.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| Arkema Group Rilsan® AZM 30 NOIR T6LD Nylon 12, 30% Glass Fiber Filled (Conditioned) Designation ISO 1874-PA12,MHLR,16-060,GF30Rigid grade with glass fiber (30%) for injection molding. Available color: black. Reinforced light and heat stabilizing agent. Mold-release agent.High rigid.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| Arkema Group Rilsan® AZM 50 NOIR T6LD Nylon 12, 50% Glass Fiber Filled (Conditioned) Designation ISO 1874-PA12,MHLR,16-090,GF50Rigid grade with glass fiber (50%) for injection molding. Available color: black. Reinforced light and heat stabilizing agent. Mold-release agent.High rigid.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D 648 |
| Shakespeare Isocor™ HW29TL Nylon 610 Isocor™ HW29TL is an ultra low viscosity PA-610 with excellent melt flow characteristics. Isocor™ HW29TL is specifically formulated for thin wall or high speed injection molding applications. .. |
|||