- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 123 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 123 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP CIP15015 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP CIP15015 UV Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® MC8100 PC+ABS (Asia Pacific) Extrusion blowmolding grade. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPHC T20050 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1212 PC Copolymer (Europe-Africa-Middle East) 18 MFR LEXAN High Flow Ductile Copolymer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer 18 MFR LEXAN High Flow Ductile Copolymer UV-stabilized, available in transparent colors only |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer (Europe-Africa-Middle East) 18 MFR LEXAN High Flow Ductile Copolymer UV-stabilized, available in transparent colors only |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1262 PC Copolymer (Asia Pacific) 19 MFR LEXAN High Flow Ductile Copolymerwith 400 nm cut off, available in transparent colors only |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® C1110 PC+ABS (Asia Pacific) High impact and ductility at 73F (23C) and -20F (-29C). |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1212 PC Copolymer (Asia Pacific) 18 MFR LEXAN High Flow Ductile Copolymer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa JH950-502 Low-temperature Resistant & Flame Retardant PC/ABS Alloy Features:UL V-0 @ 3.2mmExcellent balance propertiesGood low temperature resistanceGood normal/low temperature impact strengthGood surfaceApplications:ControllerPlugSocketShell of ammeterInformation .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | Unannealed; ASTM D648 |
| Global PP-1142-R Polypropylene Homopolymer Description-transparency, high stiffness, high heat resistantApplications-disposable drinkware, thin-walled parts, medical applicationsInformation provided by Global Polymers Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| Ineos H07N-00 Polypropylene Homopolymer Grade H07N-00 is a barefoot polypropylene homopolymer with nucleation designed for extrusion processing. This resin meets the requirements of the U.S. Food and Drug administration as specified in 12.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 1-3130 30% Talc-Filled Polypropylene Homopolymer INNOPOL® CS 1-3130 is a 30% talc-filled polypropylene homopolymer compound /PP-H TD30 (ISO 1043)/. This grade is available in natural and custom colored form as well.INNOPOL® CS 1-3130 is reco.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 2-3120 20% Talc Filled Polypropylene Block-Copolymer INNOPOL® CS 2-3120 is a 20% talc filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-3120 is developed for producing.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Lubricomp ZP003 PPE+PS (Europe-Africa-Middle East) LNP* LUBRICOMP* ZP003 is a compound based on PPE + PS Blend resin containing PTFE, Silicone. Added features include Internally Lubricated.This data was supplied by SABIC-IP for the Europe-Africa-Mid.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Xenoy® X3515 PC+POLYESTER (Asia Pacific) Flame Retardant, Impact Modified, Opaque, Designed for outdoor telecommunication enclosure applications.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ISO 75 |
| Teijin Multilon T-3011 Standard PC/ABS Polymer Alloy General grade of PC/ABS polymer alloy, having improved impact strength and heat resistance compared with a heat resistant ABS and flame retardant m-PPE and also having higher fluidity compared with .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON KD000EI Acetal Copolymer (Europe-Africa-Middle East) LNP* Stat-Kon* KD000EI is a compound based on Acetal Copolymer resin containing Carbon Powder. Added features include: Electrically Conductive, Impact Modified. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL EM6101 PPE+PS Automotive interiors. Improved flow characteristics/overall processing economy. 250F DTUL. Good property retention/wide temperature range. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | Unannealed; ASTM D648 |
| Teknor Apex Sinpolene TPP2020 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Talc Filler, 20% Filler by Weight Uses: Appliance Components; Automotive Applications; Housings Forms: Pellets Process.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE DescriptionPolyfort® FLP 3714 is a 20% glass filled HDPE product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE DescriptionPolyfort® FLP 3714 is a 20% glass filled HDPE product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE DescriptionPolyfort® FLP 3714 is a 20% glass filled HDPE product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| ExxonMobil PP1222F Mineral-filled Homopolymer Medium melt flow rate homopolymer, 20% filled. Particularly suitable for consumer products and appliance applications requiring long term heat aging resistance. UL continuous service rating of 95°.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0336M20CL Mica Reinforced Coupled |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0336M40L Mica Reinforced |
|||