- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 109 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 109 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYblend 45FS GKF2505 PC/ABS-Blend, Glass Fiber reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C @Thickness 3.20 mm |
228 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Cycoloy® C6800 PC+ABS (Asia Pacific) PC+ABS, nonchlorinated, nonbrominated flame retardant.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPC 05ENH Polypropylene Copolymer, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C @Thickness 3.20 mm |
228 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Cycoloy® C6800 PC+ABS PC+ABS, nonchlorinated, nonbrominated flame retardant.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Flint Hills P4C5B-030 Homopolymer Polypropylene Homopolymer, UL certified, and FDA compliant.Features: Nucleated, antistat, and controlled rheology.Applications: Injection molding: closures and excellent mold release.Former Huntsman polypropylene.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Flint Hills P4C6B-194 Polypropylene Homopolymer Features: Antistat, Nucleated. Product does not contain animal derived components. Phthalate-free.Applications: Injection MoldingInformation Provided by Flint Hills Resources |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 1-3610 UW Polypropylene Homopolymer INNOPOL® CS 1-3610 UW is a white colored, flame retarded and UV-stabilized polypropylene homopolymer compound.INNOPOL® CS 1-3610 UW is recommended for producing electric articles by injection .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| LyondellBasell Astryn 65F4-2 Polypropylene Homopolymer, 20% Talc Key Features: conventional melt flow, high modulus, mineral-filled polypropylene homopolymer, excellent impact and stiffness balance, good dimensional stability, excellent heat resistance, good colo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ISO Method 180 |
| LyondellBasell Astryn BB77G Polypropylene Copolymer, 15% Talc Key Features: high melt flow, high modulus, UV-stabilized, mineral-filled polypropylene copolymer, good impact stiffness and balance, good dimensional stability, good colorability, good aesthetics, .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 9710 PP SABIC® PPcompound 9710 is a mineral filled, impact modified polypropylene TPO. This material combines high impact resistance, scratch resistance, and heat stability with interior automotive UV st.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Halar® 1400LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) Low ViscosityUses: FibersAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 300 °CInformation provided by Solvay Spec.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C @Thickness 3.20 mm |
228 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON MD000AP PP LNP* STAT-KON* MD000AP is a compound based on Polypropylene containing Carbon Powder. Added features of this grade include: Electrically Conductive, Exceptional Processing. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | Unannealed; ASTM D648 |
| Styron EMERGEâ„¢ 9500CR Polycarbonate (PC) / Polyethylene Terephthalate (PET) Overview: EMERGEâ„¢ PC/PET 9500 CR advanced resin is a polycarbonate blend with excellent chemical resistance and ignition resistance properties. This grade was designed for use in medical equipm.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C @Thickness 6.40 mm |
228 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL N225X PPE+PS PPE+PS blend. Unfilled. Halogen-Free FR performance. UL94 V0/5VA. UL746C F1. Dielectric Strength. Suitable for E/E market indoor/outdoor applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM Test |
| Styrolution Terblend® N NG-02 8% Glass Filled ABS/PA6 (Dry) Terblend N NG-02 is a glass fibre reinforced ABS/PA6 blend with excellent dimensional stability, high impact strength and good surface appearance.Information provided by STYROLUTION, which is a join.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | Unannealed; ASTM D648 |
| Styron PULSEâ„¢ 2000 EZ PC/ABS Engineering Resin Overview: PULSE 2000 Engineering Resin is designed to provide top performance in tough applications, from single piece items to intricate components. Ideal for energy management solutions, it can wi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 229 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 2181HU High Flow, Fortified, Impact Resistant Polypropylene DescriptionPolyfort® FPP 2181HU is a high flow, fortified, impact resistant polypropylene, stabilized for UV resistance, and available in automotive matched colors. Information provided by A. Schul.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 229 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 2181HU High Flow, Fortified, Impact Resistant Polypropylene DescriptionPolyfort® FPP 2181HU is a high flow, fortified, impact resistant polypropylene, stabilized for UV resistance, and available in automotive matched colors. Information provided by A. Schul.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 229 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 2181HU High Flow, Fortified, Impact Resistant Polypropylene DescriptionPolyfort® FPP 2181HU is a high flow, fortified, impact resistant polypropylene, stabilized for UV resistance, and available in automotive matched colors. Information provided by A. Schul.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Eastman Tritan EX401 Copolyester Eastman Tritan EX401 is an amorphous copolyester with excellent appearance and clarity. Tritan EX401 contains a mold release derived from vegetable based sources. Its most outstanding features are.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Eastman Tritan MX810 Copolyester Applications:Blood TherapyDialyzer HousingsIV ComponentsKey Attributes:Ease of processingExcellent clarityExcellent hydrolytic stabilityFast drying timesGood chemical resistanceOutstanding impact re.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Eastman Tritan MX811 Copolyester Applications:Blood TherapyDialyzer HousingsIV ComponentsKey Attributes:Ease of processingExcellent clarityExcellent hydrolytic stabilityFast drying timesGood chemical resistanceGood heat resistanceO.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Eastman Tritan TX2001 Copolyester Eastman Tritan TX2001 is an amorphous copolyester with excellent appearance and clarity. Eastman Tritan TX2001 contains a mold release derived from vegetable based sources. Its most outstanding fe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ISO 75-1/-2 |
| Covestro Makroblend® KU 2-7608 Polycarbonate + PBT, Mineral Filled Impact Grade ISO 7792-1-PC/PBT,MHPR,-030,MD10(PC+PBT)-blendsimpact modifiedInjection molding grade 10% mineral filledPreprocessingMax. Water content |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ISO 75-2/B |
| ExxonMobil Exxtral™ CMU 236 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for automotive interior covered applications such as retainers in which a good stiffness/toughness balance is required.Availa.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Aclo Accutech Polypropylene Copolymer CP0436W30L1 Wollastonite Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Aclo Accutech Polypropylene Copolymer CP0436T30L Talc Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ASTM D648 |
| Cheng Yu Plastic A703G2 ABS 20% Glass Fiber Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C @Thickness 3.20 mm |
228 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP Cycoloy_C6303 PC+ABS LNP* Lubricomp* Cycoloy_C6303 compound is a Wear resistant (5% PTFE), flame retardant PC+ABS. High heat and good hydrolytic stability. UL listing from Japan and Pacific. |
|||