- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 106 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 106 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C @Thickness 3.18 mm |
223 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ MD 4245-59770 Polypropylene Copolymer (PP Copolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hysun™ 678UV ASA Available in North America Additive: UV Stabilizer Features: Good Impact Resistance and High Heat ResistanceRoHS CompliantForm: PelletsInformation provided by Ravago |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| PolyMirae Moplen HP552R Fiber (Staple/BCF/CF) Grade Polypropylene Moplen HP552R is the polypropylene homopolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen HP552R is a homopolymer typically used by customers in high speed p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | |
| Ineos ABS NOVODUR® KU 2-5300 ABS, Injection Grade
(discontinued **) Injection molding grade, high heat resistance and toughness, low-emission.Applications: Automotive parts, household goods.Information provided by the manufacturer.Novodur is produced by Styrolution .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | |
| Ineos ABS Lustran® H801 High heat resistance, PC modified, low emission, increased flow.,Property data per ISO test methods. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| LG Chemical SEETEC H7525 Polypropylene, Homopolymer Features: Seetec H7525 is designed for the extrusion of staple fibers. This grade is characterized by Medium MWD and good thermobonding, with anti-gas fading stabilization. SEETEC H7525 meets the FD.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| LG Chemical SEETEC H7600 Polypropylene, Homopolymer Features: Seetec H7600 is designed for the extrusion of continuous filament (CF) and staple fibers. This grade is characterized by medium MWD and good heat stability. SEETEC H7600 meets the FDA requ.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 1-3000 N DEL Polypropylene Homopolymer INNOPOL® CS 1-3000 N DEL is developed for producing injection molded automotive components.All information provided by INNO-COMP. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| IRPC Polimaxx Polene 2541TC Polypropylene Block Copolymer CHARACTERISTICS: EXCELLENT FLOWABILITY, HIGH STIFFNESS, HEAT STABILITY, HIGH IMPACTAPPLICATIONS: INJECTION MOLDING SPECIALLY FOR WASHING TUB, ELECTRICAL APPLIANCES, THIN WALL CONTAINERS |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75B |
| Lucite International Diakon® CMH454 Acrylic Polymer Information provided by Lucite International |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON AX02747 ABS LNP* STAT-KON* AX02747 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® ASA 778 UV WT168 Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Good UV ResistanceAppearance: WhiteInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C @Thickness 6.40 mm |
223 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Xenoy® 5220 PBT+PC (Asia Pacific) Unreinforced, polycarbonate-based polymer blend, excellent chemical resistance and impact.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75 |
| Styrolution Novodur® 5300 ABS Novodur 5300 is a high heat injection molding grade with high impact strength, good chemical resistance and reduced emission (PC modified)Information provided by Styrolution |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75 |
| Styrolution Novodur® H801 ABS / PC Novodur H801 is a high heat injection molding grade with high impact strength and reduced emission.Information provided by Styrolution |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | Annealed; ASTM D648 |
| Techmer ES Plastiblend® ABS HH BK MB Availability: North AmericaForms: PelletsFeatures: High Gloss and High Heat ResistanceAppearance: BlackProcessing Method: Injection MoldingInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C @Thickness 3.17 mm |
223 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Chase Plastics CP Pryme® A100HH ABS Molding Resin, High Heat Information provided by Chase Plastics. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer DescriptionPolypropylene PP 3052X-01 is an extra high flow impact resistant copolymer with relatively high stiffness. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | 0.25 inch; ASTM D648 |
| PlastxWorld CEVIAN® B14E0 PBT/ABS Alloy Excellent flowability, high impact strength and toughness. These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer DescriptionPolypropylene PP 3052X-01 is an extra high flow impact resistant copolymer with relatively high stiffness. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer DescriptionPolypropylene PP 3052X-01 is an extra high flow impact resistant copolymer with relatively high stiffness. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75-1/-2 |
| Covestro Bayblend® FR 3030 Polycarbonate + ABS, Flame Retardant Grade Flame retardant extrusion gradeVicat/B 120 temperature = 115 °Cgood extrusion and vacuum-forming behaviourUL-listing 94 V-0 (1.5 mm)halogen-free according to DIN VDE 0472-815glow wire temperature (.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75-1/-2 |
| Covestro Makroblend® KU 2-7915 Polycarbonate + PBT, Impact Grade ISO 7792-1-PC/PBT,MHPR,-020(PC+PBT)-blendsimpact modifiedInjection molding gradeexcellent toughness at low temperaturesideal for painted applicationsunreinforcedPreprocessingMax. Water content |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| Arkema Group Pebax® 7233 Polyether Block Amide (PEBA) Information provided by Arkema Group |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| Braskem H 605 Thermoforming Polypropylene Applications: Flat and corrugated sheets with high transparency; thermoformed packing with high transparency. Information provided by Braskem |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0336M10L Mica Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0336W10L Wollastonite Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| Cheng Yu Plastic A706G1 SAN, 10% Glass Fiber |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 212 Polystyrene, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ASTM D648 |
| Braskem H 605 Extrusion Polypropylene Description: H 605 is a low melt flow rate homopolymer with high transparency. This resin is designed for extrusion and thermoforming. H 605 exhibits excellent processability, high output, excellent.. |
|||