Thermal Properties | Metric | English | Comments |
---|---|---|---|
Maximum Service Temperature, Air | 160 °C @Time <=86400 sec |
320 °F @Time <=24.0 hour |
|
Murtfeldt Murinyl® Polyvinylidinefluoride As a fluorinated plastic, Murinyl® is exceptionally resistant to chemicals, hydrolysis, and sterilization. Its properties change very little at high service temperatures and after long-term exposur.. |
|||
Maximum Service Temperature, Air | 160 °C @Time <=86400 sec |
320 °F @Time <=24.0 hour |
|
Murtfeldt Murlubric® [FS] Oil Modified Nylon 6 Murlubric® is a modified cast polyamide that mineral oil is integrated into during polymerization. As a result, the material has self lubricating properties and retains its excellent characteristi.. |
|||
Maximum Service Temperature, Air | 160 °C @Time <=86400 sec |
320 °F @Time <=24.0 hour |
|
Murtfeldt Murylon® B Nylon 6 Murylon® B natural has the best impact resistance of all Murylon materials. This material is especially suited for use in machine construction thanks to an excellent combination of mechanical prope.. |
|||
Maximum Service Temperature, Air | 160 °C @Time <=180000 sec |
320 °F @Time <=50.0 hour |
IEC 60216/T1 |
Raschig Group MELOPAS® 2010 MF Melamine Organically and inorganically filled Melamine molding compound. Excellent surface hardness, good mechanical strength, good electrical properties. This product meets the allowed upper limits for heav.. |
|||
Maximum Service Temperature, Air | 160 °C @Time <=180000 sec |
320 °F @Time <=50.0 hour |
IEC 60216/T1 |
Raschig Group MELOPAS® 6605 MP Melamine Cellulose reinforced Melamine molding compound. Very good electrical properties, excellent surface hardness, good mechanical strength and heat resistance, good wear and UV-stability, good gliding be.. |
|||
Maximum Service Temperature, Air | 160 °C @Time 7.20e+7 sec |
320 °F @Time 20000 hour |
IEC 60216/T1 |
Raschig Group RALUPOL® 4566 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u.. |
|||
Maximum Service Temperature, Air | 160 °C @Time <=86400 sec |
320 °F @Time <=24.0 hour |
|
Murtfeldt Murylat® Polyethylene Terephthalate Thanks to its extremely low absorption of moisture and low expansion coefficient, Murylat® is ideally suited for the processing of precision parts. Murylat® has an extremely high hardness grade an.. |
|||
Maximum Service Temperature, Air | 160 °C @Time <=86400 sec |
320 °F @Time <=24.0 hour |
|
Murtfeldt Murylat® SP Polyethylene Terephthalate Murylat® SP combines the properties of Murylat® with improved wear and friction characteristics. It also has increased dynamic resilience which, for example, significantly reduces the required dri.. |