Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 17.3 µm/m-°C @Temperature 0.000 - 100 °C |
9.60 µin/in-°F @Temperature 32.0 - 212 °F |
|
Crucible Steel 303 Plus Chromium-Nickel Steel Crucible 303 Plus is a non-hardenable austenitic chromium-nickel steel to which elements have been added to improve machinability and non-galling characteristics. Better machinability than that of.. |
|||
CTE, linear | 17.3 µm/m-°C @Temperature 0.000 - 100 °C |
9.60 µin/in-°F @Temperature 32.0 - 212 °F |
|
Crucible Steel 303 SE Chromium-Nickel Steel Crucible 303 SE is a non-hardenable austenitic chromium-nickel steel to which selenium has been added to improve machinability and non-galling characteristics. This grade is non-magnetic in the anne.. |
|||
CTE, linear | 17.3 µm/m-°C @Temperature 0.000 - 100 °C |
9.60 µin/in-°F @Temperature 32.0 - 212 °F |
|
Crucible Steel 304L Chromium-Nickel Steel Crucible 304L is a non-hardenable, low carbon austenitic chromium-nickel steel designed for special applications. It is particularly suitable for applications requiring welding operations where it i.. |
|||
CTE, linear | 17.3 µm/m-°C @Temperature 25.6 - 316 °C |
9.60 µin/in-°F @Temperature 78.0 - 600 °F |
|
Carlson Nitronic® 50® Austenitic Stainless Steel General DescriptionNitronic 50 is a nitrogen-strengthened austenitic stainless steel that possesses corrosion resistance superior to 316, 316L, 317 and 317L plus approximately twice the yield streng.. |
|||
CTE, linear | 17.3 µm/m-°C @Temperature 25.6 - 316 °C |
9.60 µin/in-°F @Temperature 78.0 - 600 °F |
|
Carlson Nitronic® 60® Austenitic Stainless Steel General DescriptionNitronic 60 is an anti-galling and wear resistant austenitic stainless steel. It provides a significantly lower cost alternative to combat wear and galling when compared with cob.. |
|||
CTE, linear | 17.3 µm/m-°C @Temperature 25.0 - 100 °C |
9.60 µin/in-°F @Temperature 77.0 - 212 °F |
|
Carpenter Gall-Tough® Stainless Data provided by Carpenter Technology Corporation.6.4 mm diameter tensile specimens from center of 25.4 mm diameter bar annealed 1066°C 1 hour, water quenched, and ground.Threshold Galling Stress 1.. |
|||
CTE, linear | 17.3 µm/m-°C @Temperature 25.0 - 100 °C |
9.60 µin/in-°F @Temperature 77.0 - 212 °F |
|
Carpenter Gall-Tough® Stainless, Annealed and Cold Drawn Bar, 20% Cold Work Data provided by Carpenter Technology Corporation.Threshold Galling Stress 103 MPa (higher stress tests not performed). The avg. total volume loss on the wear test is 5 mm³ at 100 rpm.Gall-Tough®.. |
|||
CTE, linear | 17.3 µm/m-°C @Temperature 25.0 - 100 °C |
9.60 µin/in-°F @Temperature 77.0 - 212 °F |
|
Carpenter Gall-Tough® Stainless, Annealed and Cold Drawn Bar, 10% Cold Work Data provided by Carpenter Technology Corporation.Threshold Galling Stress 103 MPa (higher stress tests not performed). The avg. total volume loss on the wear test is 5 mm³ at 100 rpm.Gall-Tough®.. |
|||
CTE, linear | 17.3 µm/m-°C @Temperature 25.0 - 100 °C |
9.60 µin/in-°F @Temperature 77.0 - 212 °F |
|
Carpenter Gall-Tough® Stainless, Annealed and Cold Drawn Bar, 0% Cold Work Data provided by Carpenter Technology Corporation.Threshold Galling Stress 103 MPa (higher stress tests not performed). The avg. total volume loss on the wear test is 5 mm³ at 100 rpm.Gall-Tough®.. |