- Polymer Property : CTE, linear = 9.50 µin/in-°F
Polymer Property : CTE, linear = 9.50 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 800 °C |
9.50 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 800 °C |
9.50 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 800 °C |
9.50 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 800 °C |
9.50 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 800 °C |
9.50 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 900 °C |
9.50 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 900 °C |
9.50 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 900 °C |
9.50 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes HR-160® alloy, annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 900 °C |
9.50 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 900 °C |
9.50 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 900 °C |
9.50 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes HR-160® alloy, plate, aged 8000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 900 °C |
9.50 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 800 °C |
9.50 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 800 °C |
9.50 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 556® alloy, hot rolled, solution annealed plate, 6.4-12.7 mm (1/2 in.) thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 0.000 - 100 °C |
9.50 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Crucible Steel 321 Chromium-Nickel Steel Crucible 321 is a non-hardenable, low carbon austenitic chromium-nickel steel which is particularly adaptable for parts fabricated by welding without postweld annealing for use at temperatures betwe.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 20.0 - 500 °C |
9.50 µin/in-°F @Temperature 68.0 - 932 °F |
|
| ATI Allegheny Ludlum 310S Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||