Polymer Property : CTE, linear = 9.28 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.7 µm/m-°C @Temperature 23.0 - 600 °C |
9.28 µin/in-°F @Temperature 73.4 - 1110 °F |
|
| Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 23.0 - 600 °C |
9.28 µin/in-°F @Temperature 73.4 - 1110 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 23.0 - 600 °C |
9.28 µin/in-°F @Temperature 73.4 - 1110 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 5% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, 50% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 23.0 - 600 °C |
9.28 µin/in-°F @Temperature 73.4 - 1110 °F |
|
| Haynes Multimet® alloy, SMAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 0.000 - 100 °C |
9.28 µin/in-°F @Temperature 32.0 - 212 °F |
|
| CLAL-MSX CUPROROR® TL4 Hard, Copper Alloy Alloy especially suited to applications in electronics and electro technology. This doped copper, displays high electrical and thermal conductivity, good mechanical properties and excellent temperat.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 23.0 - 600 °C |
9.28 µin/in-°F @Temperature 73.4 - 1110 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 25% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||