Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, 0.71-3.2 mm thick sheet, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, 10% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, 12.7-50.8 mm thick bar, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, 20% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, 20% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, 30% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, 50% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, 60% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, all-weld metal, GMAW short arc HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, SMAW weld, C-22 base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, transverse, GMAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, transverse, GMAW spray weldment, 23.4 mm thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, transverse, GTAW weldment, sheet - plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 21.0 - 93.0 °C |
9.00 µin/in-°F @Temperature 69.8 - 199 °F |
|
Crucible Steel XM-19 Stainless Steel Crucible XM-19 Stainless is a nitrogen strengthened, low carbon, austenitic, stainless steel that provides good corrosion resistance in combination with high strength. The alloy has better corrosio.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 25.6 - 93.3 °C |
9.00 µin/in-°F @Temperature 78.0 - 200 °F |
|
Carlson Nitronic® 50® Austenitic Stainless Steel General DescriptionNitronic 50 is a nitrogen-strengthened austenitic stainless steel that possesses corrosion resistance superior to 316, 316L, 317 and 317L plus approximately twice the yield streng.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 21.0 - 927 °C |
9.00 µin/in-°F @Temperature 69.8 - 1700 °F |
|
ATI Allegheny Ludlum AL 625HP™ Stainless Steel Nickel-based superalloy. Characteristics:exceptional fatigue resistance, excellent resistance to oxidation and corrosion, outstanding strength and toughness over a range of temperatures from cryogen.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, GMAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, GMAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, GTAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, transverse, GTAW spray weldment, 12.7 mm (1/2 in.) thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, transverse, SMAW weldment, 19.1 mm thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 20.0 - 877 °C |
9.00 µin/in-°F @Temperature 68.0 - 1610 °F |
|
Kennametal Stellite Stellite® 25 Cobalt Chromium Cast Alloy Stellite alloy 25 forms a protective oxide film during hot metal-on metal wear which prevents metal transfer and damage due to adhesion. The alloy is resistant to thermal cracking and surface fatig.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, 60% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, all-weld metal, GTAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 24.0 - 982 °C |
9.00 µin/in-°F @Temperature 75.2 - 1800 °F |
|
Haynes Hastelloy® C-22® alloy, SMAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 16.2 µm/m-°C @Temperature 20.0 - 1000 °C |
9.00 µin/in-°F @Temperature 68.0 - 1830 °F |
|
Kennametal Stellite Stellite® 4 Cobalt Chromium Alloy The higher tungsten content of Stellite alloy 4 gives improved high temperature properties and an increase in abrasive wear resistance over Stellite alloy 6, but not as good as Stellite alloy 12 or .. |