Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 15.5 - 16.5 µm/m-°C @Temperature 20.0 - 200 °C |
8.61 - 9.17 µin/in-°F @Temperature 68.0 - 392 °F |
|
PEAK Werkstoff DISPAL S220 Aluminum Alloy, AlSi35, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 15.5 - 16.5 µm/m-°C @Temperature 20.0 - 200 °C |
8.61 - 9.17 µin/in-°F @Temperature 68.0 - 392 °F |
|
PEAK Werkstoff DISPAL S220 Aluminum Alloy, AlSi35, Condition O Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 0.000 - 1000 °C |
8.61 µin/in-°F @Temperature 32.0 - 1830 °F |
|
Kennametal Stellite Stellite® 6K 12.7 or 22.2 mm plate 13.3 mm^3 volume loss--abrasive wear data. Applications include agitators, augers, ball mills, banbury mills, cams, crusher bearings, dryers, dry presses, dump cars, fans, filters, food machinery, g.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 100 °C |
8.61 µin/in-°F @Temperature 68.0 - 212 °F |
|
Industeel SIRIUS 310 25% Cr - 0.6% Si Heat Resistant Stainless Steel Description: CLI SIRIUS 310 grade is a fully austenitic stainless steel containing 25% Cr, 0.6% Si and 20% Ni additions. The alloy is well known for its multi-purpose high temperature corrosion resi.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 25.0 - 600 °C |
8.61 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 25.0 - 600 °C |
8.61 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 0.000 - 900 °C |
8.61 µin/in-°F @Temperature 32.0 - 1650 °F |
|
Kennametal Stellite Stellite® 12 PM cast Applications: include vane plugs, fuel metering pins, spacer bushings, ball blanks (bearings), race blanks (bearings), diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wea.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 0.000 - 400 °C |
8.61 µin/in-°F @Temperature 32.0 - 752 °F |
|
Industeel SIRIUS 800 Heat Resistant Alloy Description: The SIRIUS® 800, H and H+ grades are three variants of a high chromium and nickel austenitic alloy which combines good corrosion and creep resistance. SIRIUS® 800 is employed at t.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet, GTAW weld HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 30.0 - 538 °C |
8.61 µin/in-°F @Temperature 86.0 - 1000 °F |
|
Haynes Hastelloy® G-30® alloy, 50% cold rolled and 1 hour at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 25.0 - 600 °C |
8.61 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 200 °C |
8.61 µin/in-°F @Temperature 68.0 - 392 °F |
|
ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 50% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co.. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 982 °C |
8.61 µin/in-°F @Temperature 68.0 - 1800 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |