Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 500 °C |
8.11 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 214® alloy, 10% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 500 °C |
8.11 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 500 °C |
8.11 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 214® alloy, 40% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 500 °C |
8.11 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 214® alloy, 50% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 500 °C |
8.11 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 500 °C |
8.11 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 214® alloy, 50% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 500 °C |
8.11 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 214® alloy, 50% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 500 °C |
8.11 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 500 °C |
8.11 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 500 °C |
8.11 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 214® alloy, 30% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 600 °C |
8.11 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 600 °C |
8.11 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 600 °C |
8.11 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 600 °C |
8.11 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 600 °C |
8.11 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 24.0 - 649 °C |
8.11 µin/in-°F @Temperature 75.2 - 1200 °F |
|
Haynes Hastelloy® C-22® alloy, 60% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 24.0 - 649 °C |
8.11 µin/in-°F @Temperature 75.2 - 1200 °F |
|
Haynes Hastelloy® C-22® alloy, GTAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 18.0 - 648 °C |
8.11 µin/in-°F @Temperature 64.4 - 1200 °F |
|
Latrobe Lescalloy® 4340 VAC-ARC ; 10.5" square High Strength Alloy Steel LESCALLOY 4340 VAC-ARC steel is a low alloy, nickel-chromium-molybdenum steel capable of being heat treated to high strength levels. The alloy has a good combination of ductility, toughness and str.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 24.0 - 100 °C |
8.11 µin/in-°F @Temperature 75.2 - 212 °F |
Mean |
Special Metals INCONEL® G-3 Nickel Superalloy Data provided by the manufacturer, Special Metals. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 20.0 - 315 °C |
8.11 µin/in-°F @Temperature 68.0 - 599 °F |
|
ATI Allegheny Ludlum AL 601™ Nickel-Base Alloy, 1149°C (2100°F) Solution Treated, UNS N06601 Allegheny Ludlum's AL 601 alloy is an austenitic nickel-chromium-iron alloy designed for both heat and corrosion resistance. As compared to AL 600 alloy, the AL 601 alloy has, in addition to increa.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 20.0 - 538 °C |
8.11 µin/in-°F @Temperature 68.0 - 1000 °F |
|
ATI Allegheny Ludlum AL 600™ Nickel-Base Alloy, UNS N06600 Allegheny Ludlum is a nickel-chromium alloy designed for use from cryogenic to elevated temperatures in the range of 1093 degrees Celsius. AL 600 alloy is non-magnetic and readily weldable. The al.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 600 °C |
8.11 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes 25 alloy, room temperature after 0% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 600 °C |
8.11 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 600 °C |
8.11 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 25.0 - 600 °C |
8.11 µin/in-°F @Temperature 77.0 - 1110 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 24.0 - 649 °C |
8.11 µin/in-°F @Temperature 75.2 - 1200 °F |
|
Haynes Hastelloy® C-22® alloy, GMAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 24.0 - 649 °C |
8.11 µin/in-°F @Temperature 75.2 - 1200 °F |
|
Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 24.0 - 649 °C |
8.11 µin/in-°F @Temperature 75.2 - 1200 °F |
|
Haynes Hastelloy® C-22® alloy, 6.4-19.1 mm thick plate, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 24.0 - 649 °C |
8.11 µin/in-°F @Temperature 75.2 - 1200 °F |
|
Haynes Hastelloy® C-22® alloy, all-weld metal, GTAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
CTE, linear | 14.6 µm/m-°C @Temperature 24.0 - 649 °C |
8.11 µin/in-°F @Temperature 75.2 - 1200 °F |
|
Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |