- Polymer Property : CTE, linear = 7.17 µin/in-°F
Polymer Property : CTE, linear = 7.17 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.9 µm/m-°C @Temperature 800 °C |
7.17 µin/in-°F @Temperature 1470 °F |
|
| Outokumpu 4742 High Temperature Ferritic Stainless Steel Good scaling resistance and can be subjected to reducing sulphur environments without risk. Subject to 475°C embrittlement and grain coarsening at temperatures above 950°C. s-phase may form afte.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 800 °C |
7.17 µin/in-°F @Temperature 1470 °F |
|
| Outokumpu 4762 High Temperature Ferritic Stainless Steel Highest chromium content-most resistant to reducing sulphurous gases. Susceptible to 475°C embrittlement and s-phase forms during long exposures in the range 600-800°C.Applications: Mostly used i.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 600 °C |
7.17 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Kennametal Stellite Nucalloy® 453 High-Silicon Nickel-Base Hardfacing Alloy Applications include chemical control valves, nuclear globe valves, nuclear gate valves, nuclear sliding parts, and pressure bars for plywood cutters.Nucalloy® alloys are unique, patented, high-s.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 0.000 - 300 °C |
7.17 µin/in-°F @Temperature 32.0 - 572 °F |
|
| Kennametal Stellite Stellite® 12 PM with P/M Processing Applications: include vane plugs, fuel metering pins, spacer bushings, ball blanks (bearings), race blanks (bearings), diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wea.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 0.000 - 400 °C |
7.17 µin/in-°F @Temperature 32.0 - 752 °F |
|
| Kennametal Stellite Stellite® 3 PM with P/M Processing Typical applications include (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) diesel engine exhaust, fluid valve seats, saw cutt.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 300 °C |
7.17 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Industeel Superplast® 400 High Hardness Mold Steel SUPERPLAST® 400 is an injection plastic mold steel pre-hardened to a high level of hardness. It is delivered at a typical hardness of 125 kg/mm2. This steel is specially adapted for heavy-duty .. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595°C (1100°F) for 2 hours Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 0.000 - 300 °C |
7.17 µin/in-°F @Temperature 32.0 - 572 °F |
|
| Kennametal Stellite Stellite® 12 Satisfactory finishing results can be obtained using carbide tipped tools. Applications include cutting plastics, rubber, paper, carpet, and wood; saw teeth, trimmer knives, carpet knives, ledger bl.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 0.000 - 300 °C |
7.17 µin/in-°F @Temperature 32.0 - 572 °F |
|
| Kennametal Stellite Stellite® 12 PM cast Applications: include vane plugs, fuel metering pins, spacer bushings, ball blanks (bearings), race blanks (bearings), diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wea.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 25 alloy, room temperature sheet after 1000 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 400 °C |
7.17 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 400 °C |
7.17 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Shielded Metal Arc Welded (SMAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 400 °C |
7.17 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 100 °C |
7.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
| HP Alloys Alloy 718, 10% Cold Worked 10% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 100 °C |
7.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
| HP Alloys Alloy 718, 15% Cold Worked, Aged 15% Cold Worked, Aged applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Int.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 100 °C |
7.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
| HP Alloys Alloy 718, 20% Cold Worked 20% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 100 °C |
7.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
| HP Alloys Alloy 718, 30% Cold Worked, Aged 30% Cold Worked, Aged applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Int.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 500 °C |
7.17 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Bohler-Uddeholm BÖHLER W403 VMR® Hot Work Tool Steel W403 VMR is a modified hot work alloy with an excellent combination of hot tensile properties and toughness. The balanced properties of this grade are not only due to chemistry modification, but to .. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 100 °C |
7.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
| HP Alloys Alloy 718, 5% Cold Worked 5% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internatio.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 205 °C |
7.17 µin/in-°F @Temperature 68.0 - 401 °F |
|
| Kennametal Stellite Stellite® 25 Cobalt Chromium Cast Alloy Stellite alloy 25 forms a protective oxide film during hot metal-on metal wear which prevents metal transfer and damage due to adhesion. The alloy is resistant to thermal cracking and surface fatig.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 200 °C |
7.17 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 25.0 - 400 °C |
7.17 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 100 °C |
7.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
| HP Alloys Alloy 718, 25% Cold Worked 25% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||