Polymer Property : CTE, linear = 7.06 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.7 µm/m-°C @Temperature 0.000 - 300 °C |
7.06 µin/in-°F @Temperature 32.0 - 572 °F |
|
| Kennametal Stellite Stellite® 3 PM cast Typical applications include (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) diesel engine exhaust, fluid valve seats, saw cutt.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 0.000 - 300 °C |
7.06 µin/in-°F @Temperature 32.0 - 572 °F |
|
| Kennametal Stellite Stellite® 3 PM with P/M Processing Typical applications include (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) diesel engine exhaust, fluid valve seats, saw cutt.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 600 °C |
7.06 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 427 °C |
7.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 427 °C |
7.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
| Haynes Hastelloy® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Plate, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 500 °C |
7.06 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 600 °C |
7.06 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature -30.0 - 70.0 °C |
7.06 µin/in-°F @Temperature -22.0 - 158 °F |
|
| Schott N-FK51A Glass Suitable for precision moldingInformation Provided by SCHOTT North America, Inc. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 20.0 - 500 °C |
7.06 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Bohler-Uddeholm BÖHLER S601 (M2 Modified) High Speed Steel For Cold Work Applications Properties: Tungs ten-molybdenum high speed steel with ex cel lent toughness and cut ting proper ties, for a wide variety of uses.Applications: Taps, twist drills, reamers, broaching tools, meta.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.06 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 500 °C |
7.06 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 427 °C |
7.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 427 °C |
7.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 21.0 - 427 °C |
7.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 12.7 µm/m-°C @Temperature 25.0 - 100 °C |
7.06 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||