- Polymer Property : CTE, linear = 6.39 µin/in-°F
Polymer Property : CTE, linear = 6.39 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.5 µm/m-°C @Temperature 25.0 - 250 °C |
6.39 µin/in-°F @Temperature 77.0 - 482 °F |
average |
| Materion E20 Beryllium/BeO Composite, 20 Volume% BeO Metal matrix composite made up principally of beryllium and crystal BeO platelets. Produced by blending the beryllium and beryllium oxide powders into a homogeneous mixture to create isotropic prop.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 100 °C |
6.39 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Industeel CLC 1.2311 Prehardened Mold Steel (300HB/30HRC) Description: CLC 1.2311 is a 300HB (30HRC) pre-hardened grade specially designed for plastic mold industry. Chromium, Molybdenum, carbon and manganese additions are optimized to have a fully martens.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 100 °C |
6.39 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Industeel CLC 1.2312 Prehardened Mold Steel (300HB/32HRC) with Improved Machinability Description: CLC 1.2312 is a chromium-manganese-molybdenum grade designed for plastic mold industry. This grade is normally delivered in a prehardened condition at a hardness level of 300HB/32HRC. T.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 93.0 °C |
6.39 µin/in-°F @Temperature 68.0 - 199 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 93.0 °C |
6.39 µin/in-°F @Temperature 68.0 - 199 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 93.0 °C |
6.39 µin/in-°F @Temperature 68.0 - 199 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 93.0 °C |
6.39 µin/in-°F @Temperature 68.0 - 199 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 93.0 °C |
6.39 µin/in-°F @Temperature 68.0 - 199 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 93.0 °C |
6.39 µin/in-°F @Temperature 68.0 - 199 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 93.0 °C |
6.39 µin/in-°F @Temperature 68.0 - 199 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 93.0 °C |
6.39 µin/in-°F @Temperature 68.0 - 199 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 427 °C |
6.39 µin/in-°F @Temperature 68.0 - 801 °F |
|
| HP Alloys Alloy B-2, Solution Treated, 20% Cold Worked Solution Treated, 20% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 0.000 - 538 °C |
6.39 µin/in-°F @Temperature 32.0 - 1000 °F |
|
| Crucible Steel 416R Chromium Stainless Steel Crucible 416R is a pre-hardened chromium stainless steel which is suitable for use in precision match-grade rifle barrels. It can be supplied in various hardness ranges according to the specific req.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 315 °C |
6.39 µin/in-°F @Temperature 68.0 - 599 °F |
|
| Crucible Steel CPM® S35VN™ Stainless Steel CPM S35VN is a martensitic stainless steel designed to offer improved toughness over CPM S30V. It is also easier to machine and polish than CPM S30V. Its chemistry has been rebalanced so that it for.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 260 °C |
6.39 µin/in-°F @Temperature 68.0 - 500 °F |
|
| Crucible Steel PM M2 Tool Steel PM M2 is an improved quality tool steel compared to conventionally produced material. The powder metallurgy process results in a homogeneous microstructure exhibiting a uniform distribution of fine .. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 21.0 - 100 °C |
6.39 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| Dura-Bar 65-45-12 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 100 °C |
6.39 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Bohler-Uddeholm BÖHLER W403 VMR® Hot Work Tool Steel W403 VMR is a modified hot work alloy with an excellent combination of hot tensile properties and toughness. The balanced properties of this grade are not only due to chemistry modification, but to .. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 23.0 - 427 °C |
6.39 µin/in-°F @Temperature 73.4 - 801 °F |
|
| Carpenter Chrome Core® 18-FM Solenoid Quality Stainless Steel, Annealed Data provided by Carpenter Technology Corporation.This is a soft ferritic material designed for operation in more corrosive environments than tolerated by 18% Cr-Fe Type 430 stainless. This new mat.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 23.0 - 427 °C |
6.39 µin/in-°F @Temperature 73.4 - 801 °F |
|
| Carpenter Chrome Core® 18-FM Solenoid Quality Stainless Steel, Stress Relieved Data provided by Carpenter Technology Corporation.This is a soft ferritic material designed for operation in more corrosive environments than tolerated by 18% Cr-Fe Type 430 stainless. This new mat.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.39 µin/in-°F @Temperature 69.8 - 199 °F |
|
| Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1100 (Heated 593°C) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 500 °C |
6.39 µin/in-°F @Temperature 68.0 - 932 °F |
|
| ATI Allegheny Ludlum Stainless Steel Free Machining Grade Type 416, Tempered at 649°C (1200°F) (UNS S41600) Allegheny Ludlum's 416 is a free-machining stainless steel specifically designed to exhibit improved machinability. These modifications retain, in so far as possible, the good mechanical properties.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 200 °C |
6.39 µin/in-°F @Temperature 392 °F |
|
| Bohler-Uddeholm BÖHLER S500(m42) High Speed Steel Description: Cobalt Molybdenum high speed steel processing high hardness, excellent cutting properties, high red hardness and good toughness. BOHLER S500 is also available in the special grade ISORA.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 500 °C |
6.39 µin/in-°F @Temperature 68.0 - 932 °F |
|
| ATI Allegheny Ludlum Stainless Steel Free Machining Grade Type 416, Tempered at 760°C (UNS S41600) Allegheny Ludlum's 416 is a free-machining stainless steel specifically designed to exhibit improved machinability. These modifications retain, in so far as possible, the good mechanical properties.. |
|||
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 93.0 °C |
6.39 µin/in-°F @Temperature 68.0 - 199 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||