Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 10.8 µm/m-°C @Temperature 20.0 - 100 °C |
6.00 µin/in-°F @Temperature 68.0 - 212 °F |
|
Kennametal Stellite Nucalloy® 488 High-Silicon Nickel-Base Hardfacing Alloy Nucalloy® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinations of hardness and toughness, similar to the cobalt base alloys . B.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 20.0 - 100 °C |
6.00 µin/in-°F @Temperature 68.0 - 212 °F |
|
Kennametal Stellite Stellite® 98M2 cast Adhesive wear test data P/M 0.58 Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 0.000 - 100 °C |
6.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
Industeel VIRGO 15.5PH 15Cr-5Ni-3Cu Precipitation Hardening Martensitic Stainless Steel (480°C (900°F) - 1 hour - air cooling) Description: Alloy VIRGO 15.5 PH is a precipitation hardening martensitic stainless steel with 15% Cr, 5% Ni, 3.5% Cu and 0.3% Nb/Cb. The grade combines high mechanical properties and medium corrosi.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 25.0 - 100 °C |
6.00 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 25.0 - 100 °C |
6.00 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 25.0 - 100 °C |
6.00 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 25.0 - 100 °C |
6.00 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 25.0 - 100 °C |
6.00 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 25.0 - 100 °C |
6.00 µin/in-°F @Temperature 77.0 - 212 °F |
|
Haynes 242® alloy, cold rolled sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 20.0 - 316 °C |
6.00 µin/in-°F @Temperature 68.0 - 601 °F |
|
Latrobe 14-4CrMo Stainless Tool Steel 14-4CrMo is a wear resistant, martensitic stainless tool steel that exhibits better corrosion resistance than Type 440C stainless steel. The molybdenum in the steel provides superior corrosion resis.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 21.0 - 204 °C |
6.00 µin/in-°F @Temperature 69.8 - 399 °F |
|
Latrobe Lescalloy® 13-8 Mo VIM-VAR Precipitation Hardening Stainless Steel Lescalloy 13-8 Mo VIM-VAR is a precipitation hardening martensitic stainless steel offering excellent fracture toughness and transverse mechanical properties coupled with the resistance to stress-co.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 20.0 - 204 °C |
6.00 µin/in-°F @Temperature 68.0 - 399 °F |
|
HP Alloys Alloy B-2, Solution Treated, 10% Cold Worked Solution Treated, 10% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 20.0 - 204 °C |
6.00 µin/in-°F @Temperature 68.0 - 399 °F |
|
HP Alloys Alloy B-2, Solution Treated, 30% Cold Worked Solution Treated, 30% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 20.0 - 204 °C |
6.00 µin/in-°F @Temperature 68.0 - 399 °F |
|
HP Alloys Alloy B-2, Solution Treated, 40% Cold Worked Solution Treated, 40% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 20.0 - 300 °C |
6.00 µin/in-°F @Temperature 68.0 - 572 °F |
|
Schott N-SF10 Glass Information Provided by SCHOTT North America, Inc. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 20.0 - 199 °C |
6.00 µin/in-°F @Temperature 68.0 - 390 °F |
|
EDRO UltraChem® #15 Precipitation Hardening Stainless Mold Steel Ultrachem® is a chromium-nickel precipitation-hardening stainless steel, a modified PH alloy grade, which is characterized by: exceptional corrosion resistance, uniform hardness in all dimensions, .. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 21.1 - 93.3 °C |
6.00 µin/in-°F @Temperature 70.0 - 200 °F |
A and H900 |
Crucible Steel 15-5 Precipitation Hardening Stainless Steel Crucible 15-5 is a Premium Quality precipitation-hardening stainless steel which is capable of high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is a V.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature -17.8 - 316 °C |
6.00 µin/in-°F @Temperature 0.000 - 600 °F |
|
Crucible Steel 440A Chromium Steel Crucible 440A is a hardenable chromium steel which is the toughest of the high chromium cutlery grades. This grade is magnetic at all times. Information provided by Crucible Specialty Metals. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 26.7 - 538 °C |
6.00 µin/in-°F @Temperature 80.0 - 1000 °F |
|
Crucible Steel 440B Chromium Steel Crucible 440B Is a hardenable chromium steel which is cutlery grade having high attainable hardness and toughness. This grade is magnetic at all times. Information provided by Crucible Specialty Me.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 0.000 - 316 °C |
6.00 µin/in-°F @Temperature 32.0 - 600 °F |
|
Crucible Steel 440C Chromium Steel Crucible 440C is a hardenable chromium steel. It has one of the highest attainable hardnesses of the corrosion and heat resisting grades. This grade is magnetic at all times.Information provided b.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.00 µin/in-°F @Temperature 69.8 - 199 °F |
|
AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition A AK Steel 15-5 PH® provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, .. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.00 µin/in-°F @Temperature 69.8 - 199 °F |
|
AK Steel 17-4 PH® Precipitation Hardening Stainless Steel, Condition A AK Steel 17-4 PH® provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 24.0 - 260 °C |
6.00 µin/in-°F @Temperature 75.2 - 500 °F |
|
Carpenter AerMet®-for-Tooling Tool Steel, Double Aged 468°C Data provided by Carpenter Technology Corporation.This is a double vacuum melted alloy with high hardness and strength combined with exceptional ductility and toughness. The alloy is designed for c.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 20.0 - 400 °C |
6.00 µin/in-°F @Temperature 68.0 - 752 °F |
|
Assab Steels ASSAB XW-5 Cold Work Steel ASSAB XW-5 is a high-carbon, high chromium tool steel alloyed with tungsten, characterized by:High wear resistanceHigh compressive strengthHigh surface hardness after hardeningGood through-hardening.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 20.0 - 200 °C |
6.00 µin/in-°F @Temperature 68.0 - 392 °F |
|
Assab Steels VANADIS 4 Cold Work Steel VANADIS 4 is a chromium-molybdenum-vanadium alloyed steel which is characterized by:High wear resistanceHigh compressive strengthVery good through-hardening propertiesVery good toughnessExcellent di.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 20.0 - 700 °C |
6.00 µin/in-°F @Temperature 68.0 - 1290 °F |
|
ATI Allegheny Ludlum Type AL 441HP™ Stainless Steel Alloy Allegheny Ludlum stainless Type AL 441HP™ alloy is a heat resisting ferritic grade providing good oxidation and corrosion resistance for applications like automotive exhaust system components. Dua.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 24.0 - 260 °C |
6.00 µin/in-°F @Temperature 75.2 - 500 °F |
|
Carpenter AerMet®-for-Tooling Tool Steel, Double Aged 482°C Data provided by Carpenter Technology Corporation.This is a double vacuum melted alloy with high hardness and strength combined with exceptional ductility and toughness. The alloy is designed for c.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.00 µin/in-°F @Temperature 69.8 - 199 °F |
|
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Annealed Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 21.0 - 93.0 °C |
6.00 µin/in-°F @Temperature 69.8 - 199 °F |
|
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 900 (Age-Hardened 482°C/1hr/AC) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
CTE, linear | 10.8 µm/m-°C @Temperature 24.0 - 93.0 °C |
6.00 µin/in-°F @Temperature 75.2 - 199 °F |
H900 Condition |
Carpenter Custom 450® Stainless Steel, Condition H1050 (Age Hardened 566°C) Data provided by Carpenter Technology Corporation.Custom 450® stainless is a martensitic age-hardenable stainless steel which exhibits very good corrosion resistance (similar to that of Stainless T.. |