- Polymer Property : CTE, linear = 5.00 µin/in-°F
Polymer Property : CTE, linear = 5.00 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 9.00 - 13.0 µm/m-°C @Temperature -40.0 - 125 °C |
5.00 - 7.23 µin/in-°F @Temperature -40.0 - 257 °F |
X/Y; IPC-TM-650.2.4.41 |
| Park Electrochemical Nelco® N4000-13 SI® High-Speed Multifunctional Epoxy Laminate and Prepreg The Nelco® N4000-13 series is an enhanced epoxy resin system engineered to provide both outstanding thermal and high signal speed / low signal loss properties. N4000-13 SI® is excellent for applic.. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 100 - 200 °C |
5.00 µin/in-°F @Temperature 212 - 392 °F |
Axial; ASTM E831 |
| Solvay Specialty Polymers Ryton® R-4-230NA Polyphenylene Sulfide Compound
(Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-4-230NA is an advanced 40% fiberglass reinforced polyphenylene sulfide compound which provides reduced flash and improved processability compare.. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 100 - 200 °C |
5.00 µin/in-°F @Temperature 212 - 392 °F |
Axial; ASTM E831 |
| Solvay Specialty Polymers Ryton® R-4-230BL Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4-230BL is an advanced 40% fiberglass reinforced polyphenylene sulfide compound which provides reduced flash and improved processability compared to oth.. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 100 - 200 °C |
5.00 µin/in-°F @Temperature 212 - 392 °F |
Axial; ASTM E831 |
| Chevron Phillips Ryton® R10-110BL Polyphenylene Sulfide Compound
(discontinued **) Black Polyphenylene Sulfide CompoundRyton® R10-110BL is a glass and mineral filled polyphenylene sulfide compound which provides a good combination of mechanical and electrical properties.Applicati.. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 450 °C |
5.00 µin/in-°F @Temperature 68.0 - 842 °F |
|
| H.C. Starck WCu 80/20 Tungsten-Copper Composite Material Description of Product: Tungsten-copper composite materials are produced by copper infiltration of porous sintered tungsten. They are available with different copper contents (10 - 30 %). A therm.. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 300 °C |
5.00 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Schott BG4 Band Pass Filter Ionically colored glass. Data provided by the manufacturer, Schott Glas Mainz. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 300 °C |
5.00 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Schott N-BAK2 Glass Information Provided by SCHOTT North America, Inc. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature -30.0 - 70.0 °C |
5.00 µin/in-°F @Temperature -22.0 - 158 °F |
|
| Schott N-SF6 Glass Information Provided by SCHOTT North America, Inc. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 300 °C |
5.00 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Schott SF5 Glass Information Provided by SCHOTT North America, Inc. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 300 °C |
5.00 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Schott SF6 Glass Information Provided by SCHOTT North America, Inc. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 300 °C |
5.00 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Schott SF6HT Glass Information Provided by SCHOTT North America, Inc. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 300 °C |
5.00 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Schott UG11 Band Pass Filter Ionically colored glass. Data provided by the manufacturer, Schott Glas Mainz. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 20.0 - 1000 °C |
5.00 µin/in-°F @Temperature 68.0 - 1830 °F |
DIN EN 821-1 |
| CeramTec DN 70 Dispersion Ceramic, Al2O3-ZrO2 DN 70 is a ZTA Alumina Toughened Zirconia. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
| TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod Medium To High Strength General-Purpose Alloy. Tensile property data below is typical of rod; more specific form/thickness entries are also available in MatWeb.Industry Specifications: USA Aeros.. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
| TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod or Thickness, Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to Rod or Thickness, |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
| TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod or Thickness, Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to Rod or Thickness, |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
| TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Sheet Medium To High Strength General-Purpose Alloy. Tensile property data below is typical of sheet; more specific form/thickness entries are also available in MatWeb.Industry Specifications: USA Aero.. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
| TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5), >0.500-1.000 in, STD, Per Mil-T-9047G Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to >0.500-1.000 in, STD, Per Mil-T-9047G; other specific form/thickness entries are also available i.. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
| TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5), >1.000-1.500 in, STD, Per Mil-T-9047G Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to >1.000-1.500 in, STD, Per Mil-T-9047G; other specific form/thickness entries are also available i.. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
| TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5), Rod, Square, or Hex, >2.000-3.000 in, Per Mil-T-9047G Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to Rod, Square, or Hex, >2.000-3.000 in, Per Mil-T-9047G; other specific form/thickness entries are .. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
| TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed; 1.75 - 2.50 in Rod or Thickness; Per ASTM F136) Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to this MatWeb entry; other specific form/thickness entries are also available in MatWeb.Features: A.. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
| TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Solution Treated; 0.025 - 1.000 in Sheet and Plate; Per ASTM B265) Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to this MatWeb entry; other specific form/thickness entries are also available in MatWeb.Features: A.. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 0.000 - 100 °C |
5.00 µin/in-°F @Temperature 32.0 - 212 °F |
|
| TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5), Rod, Square, or Hex, >1.500-2.000 in, Per Mil-T-9047G Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to Rod, Square, or Hex, >1.500-2.000 in, Per Mil-T-9047G; other specific form/thickness entries are .. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 21.0 - 100 °C |
5.00 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| Dura-Bar G2 Continuously Cast Gray Iron Bar Stock ASTM A48 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as an alternative to gray i.. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 21.0 - 93.0 °C |
5.00 µin/in-°F @Temperature 69.8 - 199 °F |
|
| AK Steel PH 15-7 Mo® Precipitation Hardening Stainless Steel, Condition RH 950 AK Steel 15-7 Mo® provides high strength and hardness, good corrosion resistance and minimum distortion on heat treatment. It is easily formed in the annealed condition and develops effective bala.. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 50.0 - 150 °C |
5.00 µin/in-°F @Temperature 122 - 302 °F |
x direction; IPC TM-650 2.4.41 |
| Arlon AD300C Commercial Microwave and RF Laminate Material Excellent Thermal Coefficient of Dielectric Constant (TCEr = -25 ppm/°C)Excellent PIM performanceHigh Thermal Conductivity ideal for Higher Power DesignsReduced Coefficient of Thermal Expansion in .. |
|||
| CTE, linear | 9.00 µm/m-°C @Temperature 250 °C |
5.00 µin/in-°F @Temperature 482 °F |
|
| Ceramic Process Systems AlSiC-8, 70 vol% SiC Aluminum alloy A356.2 used. Hermeticity < 1x109 atm-cc/s He.CPS fabricates AlSiC by preparing an SiC preform which is subsequently infiltrated by molten aluminum metal. After infiltration, compone.. |
|||