Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 230 µm/m-°C @Temperature 22.0 - 260 °C |
128 µin/in-°F @Temperature 71.6 - 500 °F |
|
DuPont Performance Polymers Kalrez® 1058 FFKM Perfluoroelastomer
(discontinued **) A carbon black-filled compound that has been plasticized with perfluorinated oil. It is the softest, lowest modulus compound in the Kalrez line. Generally it is similar in resistance to Compound 1.. |
|||
CTE, linear | 230 µm/m-°C @Temperature 70.0 °C |
128 µin/in-°F @Temperature 158 °F |
|
Arkema Group KYNAR FLEX® 3120-50 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Flexible, 150°C temperature rating. High stability in harsh thermal, chemical and ultraviolet environments. High toughness a.. |
|||
CTE, linear | 230 µm/m-°C @Temperature 22.0 - 260 °C |
128 µin/in-°F @Temperature 71.6 - 500 °F |
|
DuPont Performance Polymers Kalrez® 1050LF FFKM Perfluoroelastomer A general-purpose compound for O-rings, seals, and other parts used in chemical process industries. It has good hot water/steam, excellent amine resistance, and enhanced compression set properties... |
|||
CTE, linear | 230 µm/m-°C @Temperature 22.0 - 260 °C |
128 µin/in-°F @Temperature 71.6 - 500 °F |
|
DuPont Performance Polymers Kalrez® 4079 FFKM Perfluoroelastomer A low compression set compound for general-purpose use in O-rings, diaphragms, seals, and other parts used in the process and aircraft industries. It is a carbon black-filled compound with excellen.. |
|||
CTE, linear | 230 µm/m-°C @Temperature 22.0 - 260 °C |
128 µin/in-°F @Temperature 71.6 - 500 °F |
|
DuPont Performance Polymers Kalrez® 3018 FFKM Perfluoroelastomer
(discontinued **) A carbon black-filled compound that is similar to Compound 1050LF, except for higher hardness/modulus. Best hot water/steam resistance. Generally used in oil fields and process industry application.. |