Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 16.3 - 17.3 µm/m-°C @Temperature 20.0 - 300 °C |
9.06 - 9.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S220 Aluminum Alloy, AlSi35, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 16.3 - 17.3 µm/m-°C @Temperature 20.0 - 300 °C |
9.06 - 9.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S220 Aluminum Alloy, AlSi35, Condition O Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 16.3 - 17.3 µm/m-°C @Temperature 20.0 - 300 °C |
9.06 - 9.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S226 Aluminum Alloy, AlSi30CuMg, Condition T6 Heat Treatment Condition T6 (Quench in water at RT)abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of p.. |
|||
CTE, linear | 16.3 - 17.3 µm/m-°C @Temperature 20.0 - 300 °C |
9.06 - 9.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 16.3 - 17.3 µm/m-°C @Temperature 20.0 - 300 °C |
9.06 - 9.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition T6 Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
CTE, linear | 16.3 - 17.3 µm/m-°C @Temperature 20.0 - 300 °C |
9.06 - 9.61 µin/in-°F @Temperature 68.0 - 572 °F |
|
PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition T4 Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |