- Polymer Property : CTE, linear = 15.1 µm/m-°C
Polymer Property : CTE, linear = 15.1 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.1 µm/m-°C @Temperature 20.0 - 800 °C |
8.39 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Kennametal Stellite Stellite® 19 Can be machined with carbide tipped tools, but when hardness exceeds Rc55 it is best to grind. Applications include cutting tools, bearing races, guide rolls, and nozzle discs. Excellent resistance .. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 0.000 - 1000 °C |
8.39 µin/in-°F @Temperature 32.0 - 1830 °F |
|
| Kennametal Stellite Stellite® STAR cast Applications: Vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, wear pads, pins, balls, hardfa.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, cold worked sheet, 20 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
| Haynes Ultimet® alloy, all-weld metal, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
| Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 50% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, bar, after 0 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 24.0 - 500 °C |
8.39 µin/in-°F @Temperature 75.2 - 932 °F |
Mean |
| Special Metals INCONEL® G-3 Nickel Superalloy Data provided by the manufacturer, Special Metals. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||