Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 13.7 µm/m-°C @Temperature 20.0 - 900 °C |
7.61 µin/in-°F @Temperature 68.0 - 1650 °F |
|
Kennametal Stellite Stellite® 98M2 cast Adhesive wear test data P/M 0.58 Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 230® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 230® alloy, 20% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 230® alloy, 30% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 750 °C |
7.61 µin/in-°F @Temperature 77.0 - 1380 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed, 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 205 °C |
7.61 µin/in-°F @Temperature 77.0 - 401 °F |
|
Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 205 °C |
7.61 µin/in-°F @Temperature 77.0 - 401 °F |
|
Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 750 °C |
7.61 µin/in-°F @Temperature 77.0 - 1380 °F |
|
Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 750 °C |
7.61 µin/in-°F @Temperature 77.0 - 1380 °F |
|
Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 205 °C |
7.61 µin/in-°F @Temperature 77.0 - 401 °F |
|
Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 21.1 - 649 °C |
7.60 µin/in-°F @Temperature 70.0 - 1200 °F |
|
Crucible Steel LABELLE® Silicon #2 Tool Steel LaBelle Silicon #2 is a shock resisting tool steel capable of maximum toughness at relatively high hardness. It has excellent resistance to impact and battering, with good edge retention.Information.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 20.0 - 540 °C |
7.61 µin/in-°F @Temperature 68.0 - 1000 °F |
|
Crucible Steel S7 (AISI S7) Tool Steel Crucible S7 is a shock resisting tool steel with excellent toughness and high strength, along with low to medium wear resistance. It has been widely used for many years to make chisels and punches w.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 21.0 - 900 °C |
7.61 µin/in-°F @Temperature 69.8 - 1650 °F |
Mean |
Dura-Bar 120-90-02 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 21.0 - 900 °C |
7.61 µin/in-°F @Temperature 69.8 - 1650 °F |
Mean |
Dura-Bar 60-40-18 Continuously Cast Ductile Iron Bar Stock ASTM A536, 4018 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 20.0 - 100 °C |
7.60 µin/in-°F @Temperature 68.0 - 212 °F |
|
Carlson 2205 (UNS S32205) Duplex Stainless Steel General DescriptionCarlson Alloy 2205 is a second-generation, nitrogen-alloyed duplex stainless steel (ferritic-austenitic). It offers an excellent combination of both strength and corrosion resist.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 21.1 - 427 °C |
7.60 µin/in-°F @Temperature 70.0 - 800 °F |
|
Carlson C 625 Nickel-Chromium-Molybdenum Alloy General DescriptionCarlson Alloy C 625 is a nickel-chromium-molybdenum alloy that combines high strength and oxidation resistance with excellent corrosion resistance. C 625 exhibits exceptional fat.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 20.0 - 540 °C |
7.61 µin/in-°F @Temperature 68.0 - 1000 °F |
|
Crucible Steel S7 XL (Premium AISI S7) Tool Steel Crucible S7XL is a double refined, high purity grade of S7. The remelt operation produces a cleaner steel with a more uniform microstructure, offering the following advantages over conventional S7:B.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 21.1 - 302 °C |
7.60 µin/in-°F @Temperature 70.0 - 575 °F |
|
Schmolz + Bickenbach Formadur® 2312 (Ultra Holder) Plastic Mold Steel Description: Formadur® 2312 is a pre-hardened single melt Extra Fine Structure (EFS) plastic mold steel and Re-sulphurized to improve machinabilityCharacteristics: Excellent machinability compared .. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 25.0 - 400 °C |
7.61 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 230® alloy, 50% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
CTE, linear | 13.7 µm/m-°C @Temperature 21.0 - 538 °C |
7.61 µin/in-°F @Temperature 69.8 - 1000 °F |
|
Latrobe LSS™ P20 Mold Steel (ASTM P20) TLS P20 mold steel is a versatile, low-alloy tool steel that is characterized by good toughness at moderate strength levels. The steel is commonly used for plastic injection mold cavities and toolin.. |