- Polymer Property : CTE, linear = 13.1 µm/m-°C
Polymer Property : CTE, linear = 13.1 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.1 µm/m-°C @Temperature 0.000 - 600 °C |
7.28 µin/in-°F @Temperature 32.0 - 1110 °F |
|
| Kennametal Stellite Stellite® 3 PM with P/M Processing Typical applications include (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) diesel engine exhaust, fluid valve seats, saw cutt.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 800 °C |
7.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes Hastelloy® B-3® alloy, 0% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 500 °C |
7.28 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 500 °C |
7.28 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Sheet Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 500 °C |
7.28 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Plate, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 500 °C |
7.28 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Sheet, Cold-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 500 °C |
7.28 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Sheet, Cold-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 300 °C |
7.28 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Schott BG39 Band Pass Filter Ionically colored glass. Data provided by the manufacturer, Schott Glas Mainz. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 21.1 - 427 °C |
7.30 µin/in-°F @Temperature 70.0 - 800 °F |
|
| Crucible Steel CSM® 21 17Cr-4Ni Precipitation Hardening Stainless Steel CSM 21 is a precipitation hardening stainless mold steel, providing outstanding corrosion resistance and toughness, good polishability, and moderate wear resistance, combined with simple heat treatm.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 21.1 - 649 °C |
7.30 µin/in-°F @Temperature 70.0 - 1200 °F |
|
| Crucible Steel HALCOMB® 218 Tool Steel, AISI H11 Halcomb 218 is a general purpose hot work tool steel, combining good toughness with moderate high-temperature strength and heat check resistance. Because of its high toughness, it is particularly su.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 599 °C |
7.30 µin/in-°F @Temperature 1110 °F |
hardened to 45 HRC |
| Bohler-Uddeholm ORVAR® 2M / AISI H13 Hot Work Tool Steel Orvar 2 Microdized is a chromium-molybdenum-vanadium alloyed steelORVAR® 2M / AISI H13 is a conventionally produced hot work tool steel with overall good ductility, toughness, wear resistance, hard.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 27.0 - 649 °C |
7.28 µin/in-°F @Temperature 80.6 - 1200 °F |
|
| Carpenter No. 883® Hot Work Die Steel (Red-Tough) (AISI H13) No. 883 hot work die steel is a 5% chromium hot work tool steel designed particularly for applications requiring extreme toughness combined with good red-hardness. It has given an extra margin of sa.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 24.0 - 649 °C |
7.28 µin/in-°F @Temperature 75.2 - 1200 °F |
|
| Carpenter Extendo-Die® Hot Work Die Steel, Tempered 621°C Data provided by Carpenter Technology Corporation.This steel combines extreme toughness with good red hardness in large section sizes. This alloy may also be considered for many cold work applicati.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 538 - 649 °C |
7.30 µin/in-°F @Temperature 1000 - 1200 °F |
|
| Crucible Steel PDCQ Premium Quality High Toughness H13 Steel Crucible PDCQ™ is a premium version of H13, manufactured to exceed die casting industry specifications. PDCQ has at least 10 ft. lbs room temperature transverse toughness. Its enhanced toughness pr.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 20.0 - 427 °C |
7.28 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 25.0 - 200 °C |
7.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| CTE, linear | 13.1 µm/m-°C @Temperature 21.0 - 316 °C |
7.28 µin/in-°F @Temperature 69.8 - 601 °F |
|
| Latrobe LSS™ A6 Tool Steel (ASTM A6) TLS A6 tool steel is a medium-alloy, air-hardening tool steel that is characterized by its ability to be through hardened while using the low austenitizing temperatures which are typically associate.. |
|||