Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
TMA; ASTM E831 |
LNP Thermocomp® LF-1006 EM Polyetheretherketone, Glass Fiber Reinforcement
(discontinued **) Features: Good MoldabilityForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are st.. |
|||
CTE, linear, Transverse to Flow | 36.0 - 125 µm/m-°C | 20.0 - 69.4 µin/in-°F | Average value: 77.1 µm/m-°C Grade Count:18 |
Overview of materials for Acetal Copolymer, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% ar.. |
|||
CTE, linear, Transverse to Flow | 36.0 - 60.0 µm/m-°C | 20.0 - 33.3 µin/in-°F | Average value: 50.3 µm/m-°C Grade Count:14 |
Overview of materials for Polycarbonate, Carbon Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Carbon Fiber Reinforced". Each property range of values reported is minimum and maximum v.. |
|||
CTE, linear, Transverse to Flow | 36.0 - 70.0 µm/m-°C @Temperature 50.0 - 300 °C |
20.0 - 38.9 µin/in-°F @Temperature 122 - 572 °F |
Average value: 51.9 µm/m-°C Grade Count:10 |
Overview of materials for Polyimide This property data is a summary of similar materials in the MatWeb database for the category "Polyimide". Each property range of values reported is minimum and maximum values of appropriate MatWeb e.. |
|||
CTE, linear, Transverse to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ASTM D696 |
Kuraray Genestarâ„¢ G1500A-M61 Nylon, 50% Glass Filled 50% Glass reinforced injection grade. Main Features:High strengthHeat resistanceExamples of applications:Structural partsSteel alternating parts |
|||
CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
20.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP LUBRICOMP JCL36 PES (Europe-Africa-Middle East) LNP* LUBRICOMP* JCL36 is a compound based on Polyethersulfone resin containing Carbon Fiber, PTFE. Added features include : Internally Lubricated, Electrically Conductive. |
|||
CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
20.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
SABIC Innovative Plastics LNP LUBRICOMP LFL36E PEEK LNP* LUBRICOMP* LFL36E is a compound based on Polyetheretherketone containing 30% Glass Fiber, 15% PTFE. Added features of this material are: Wear Resistant, Easy Molding. |
|||
CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
20.0 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
SABIC Innovative Plastics ULTEM 3452 PEI (Europe-Africa-Middle East) 45% Glass fiber and mineral filled, enhanced flow Polyetherimide (Tg 217C) with enhanced dimensional stability. Resin is RoHS compliant. UL94 V0 and 5VA listing in recognized colors. |
|||
CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature -40.0 - 150 °C |
20.0 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
SABIC Innovative Plastics LNP THERMOCOMP EC008PXQ PEI LNP* THERMOCOMP* EC008PXQ is a compound based on Polyetherimide containing 40% Carbon FIber. Added features include: Electrically Conductive, Exceptional Processing |
|||
CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
20.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP THERMOCOMP UFW49RS PPA (Europe-Africa-Middle East) LNP* Thermocomp* UFW49RS is a compound based on Polyphthalamide resin containing Glass Fiber, Mineral. Added features of this material include: Heat Stabilized. |
|||
CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
20.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP THERMOCOMP UFW49RSC PPA (Europe-Africa-Middle East) LNP* THERMOCOMP* UFW49RSC is a compound based on Polyphthalamide resin containing Glass Fiber, Mineral. Added features include: Heat Stabilized. |
|||
CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
20.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
SABIC Innovative Plastics LNP LUBRICOMP WCL36 PBT LNP* LUBRICOMP* WCL36 is a compound based on PBT resin containing 30% Carbon Fiber, 15% PTFE. Added features of this grade include: Electrically Conductive, Wear Resistant. |
|||
CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
20.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
SABIC Innovative Plastics LNP THERMOCOMP RX98372H PA 66 LNP* Thermocomp* RX98372H is a compound based on Nylon 66 resin containing Proprietary Fillers. Characteristics of this grade are: Healthcare. |
|||
CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature 150 °C |
20.0 µin/in-°F @Temperature 302 °F |
ASTM E 228 |
DuPont Performance Polymers VESPEL TP-8556 Polyimide Thermoplastic parts from filled PI (polyimide) for balanced mechanical properties and low wear and friction performance in high temperature hostile environmentsInformation provided by DuPont Perform.. |
|||
CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
20.0 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 |
DuPont Performance Polymers Zytel® HTN FR55G50NHLW BK046 Polyphthalamide (PPA)
(Unverified Data**) 55% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide with Low Warpage and High Stiffness Zytel HTNFR55G50NHLW BK046 is a 50% glass reinforced flame retardant high perf.. |
|||
CTE, linear, Transverse to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ISO 11359 |
BASF Ultramid® B3WGM24 BK30564 10/20% Glass/Mineral Filled PA6 (Dry) Ultramid B3WGM24 BK30564 is a 30% glass/mineral filled heat stabilized injection molding PA6 grade for industrial articles having medium to high rigidity and high dimensional stability. |
|||
CTE, linear, Transverse to Flow | 36.0 - 110 µm/m-°C | 20.0 - 61.1 µin/in-°F | Average value: 59.8 µm/m-°C Grade Count:3 |
Overview of materials for Polyetheretherketone, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Glass Fiber Filled". Each property range of values reported is minimum and maximum.. |
|||
CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
TMA; ASTM E831 |
LNP Thermocomp® JF-1006 E LE BK8-055 Polyethersulfone, Glass Fiber Reinforcement
(discontinued **) Features: High Viscosity, Low ExtractablesForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many L.. |
|||
CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Thickness 1.60 mm |
20.0 µin/in-°F @Thickness 0.0630 in |
ASTM D696 |
E-Polymers SEPAZ® C230GI 30% Glass Fiber Reinforced Good Impact LCP Resin Liquid Crystal Polymer Resin: SEPAZ LCP resin has a unique structure and performance unthought of in a traditional plastics. Beside SEPAZ LCP takes the excels in all-around performance and molding .. |