- Polymer Property : CTE, linear, Transverse to Flow = 45.0 µm/m-°C
Polymer Property : CTE, linear, Transverse to Flow = 45.0 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C | 25.0 µin/in-°F | Average below Tg, Result based on 450GL30; ISO 11359 |
| Victrex® PEEK 450GL30 Polyetheretherketone, 30% Glass Fiber, Black Product Description: High performance thermoplastic material, 30% glass fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, Standard viscos.. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
|
| Cookson Group Plaskon® S-7LA Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A low stress, low alpha emission molding compound designed for packaging stress-sensitive memory devices. It offers an alpha par.. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C |
25.0 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F |
x-axis; IPC-TM 650-2.4.24 |
| Industrial Laminates/Norplex NP159 Synthetic Fabric
(discontinued **) Description: Woven aramid fiber fabric combined with high temperature phenolic resin. With a proper post baking procedure, NP159 will withstand continuous operation at 200° C. Material becomes brit.. |
|||
| CTE, linear, Transverse to Flow | 45.0 - 68.0 µm/m-°C | 25.0 - 37.8 µin/in-°F | Average value: 54.5 µm/m-°C Grade Count:4 |
| Overview of materials for Nylon 66, 10% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Mineral Filled". Specific grades with primary filler content between 5% and 14% are includ.. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C | 25.0 µin/in-°F | ASTM D696 |
| Kuraray Genestarâ„¢ G1352A-M41 Nylon, 35% Glass Filled Low friction reinforced injection grade.Main Features:Low friction coefficientAbrasion resistanceExamples of applications:Friction and wear applicationGear and wheel |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 23.0 - 150 °C |
25.0 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| SABIC Innovative Plastics ULTEM 2400 PEI (Europe-Africa-Middle East) 40% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 23.0 - 150 °C |
25.0 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| SABIC Innovative Plastics ULTEM 2400F PEI (Europe-Africa-Middle East) 40% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 listing. US FDA and European Food Contact approved. Effective June, 2007 this grade will no longer be.. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 23.0 - 150 °C |
25.0 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| SABIC Innovative Plastics ULTEM 2410 PEI (Europe-Africa-Middle East) 40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 23.0 - 150 °C |
25.0 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| SABIC Innovative Plastics Ultem PW2400 PEI (Europe-Africa-Middle East) 40% Glass fiber filled, standard flow Polyetherimide (Tg 217°C). Product designed and certified for use in Potable Water
applications. KTW, WRAS, ACS certified. NSF61 and W270 pending. US FDA and.. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
25.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP STAT-KON EX11402 PEI LNP* STAT-KON* EX11402 is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
25.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| SABIC Innovative Plastics LNP Thermocomp JF003L PES LNP* Thermocomp* JF003L is a compound based on Polyethersulfone (PES) containing Glass Fiber. Characteristics of this grade are Low Extractable.This data was supplied by SABIC-IP for the Americas r.. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
25.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP THERMOCOMP OF006 PPS - Linear LNP* THERMOCOMP* OF006 is a compound based on Linear PPS containing 30% Glass Fiber. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
25.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP THERMOCOMP OF008 PPS - Linear (Europe-Africa-Middle East) LNP* Thermocomp* OF008 is a compound based on PPS - Linear resin containing Glass Fiber. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| SABIC Innovative Plastics LNP VERTON MV006S PP (Asia Pacific) LNP VERTON* MV006S is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| SABIC Innovative Plastics LNP VERTON MV006S PP (Europe-Africa-Middle East) LNP VERTON* MV006S is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| SABIC Innovative Plastics LNP VERTON MV006SU PP (Europe-Africa-Middle East) LNP VERTON* MV006SU is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
25.0 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| SABIC Innovative Plastics NORYL CTI2550 PPE+HIPS (Europe-Africa-Middle East) NORYL CTI2550 is a glass/mineral filled material with a Vicat B/120 of 160 °C according ISO 306. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
TMA |
| Vyncolit X6151 Novolac Phenolic Glass fiber and mineral filled phenolic molding compound with excellent mechanical and thermal properties. Highest impact, high strain to failure, glycol resistant.USES: Water pumps and water pump .. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
TMA |
| Vyncolit X640 Resole Phenolic Glass fiber filled phenolic molding compound with excellent mechanical and thermal properties.USES: Information provided by Vyncolit, a Sumitomo Bak Group |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
TMA |
| Vyncolit X680 Novolac Phenolic Glass fiber and glass bead filled phenolic molding compound with excellent mechanical and thermal properties. Easily transformed into complex shapes. UL listed.USES: Complex precision parts with t.. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
TMA |
| Vyncolit X689 Novolac Phenolic Glass fiber filled and molybdeendisulfide modified phenolic molding compound with excellent mechanical and thermal properties and lower thermal expansion coefficient. It has excellent friction prop.. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C | 25.0 µin/in-°F | dry; ISO 11359-1/-2 |
| DSM Stanyl® 46SF5030 PA46-GF30 FR(17) 30% Glass Reinforced, Heat Stabilized, Flame Retardant, High Flow |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C | 25.0 µin/in-°F | dry; ISO 11359-1/-2 |
| DSM Stanyl® SC50 PA46-GF30 FR 30% Glass Reinforced, Flame Retardant, Halogen free and free of red phosphorous |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C | 25.0 µin/in-°F | ISO 11359-1/-2 |
| EMS-Grivory Grivory® HTV-45H1 black 9205 PA6T/6I-GF45 Product description: Grivory HTV-45H1 black 9205 is a 45% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Polymer designation a.. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
25.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Eurostar Starflam AFR682A1 PA66, Mineral Reinforced, Flame Retardant, Injection Molding Starflam AFR682A1 is a Flame Retardant, Mineral Filled Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
25.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Eurostar Starflam AFR682B1 PA66, Mineral Reinforced, Flame Retardant, Injection Molding Starflam AFR682B1 is a Flame Retardant, Mineral Filled Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C | 25.0 µin/in-°F | ISO 11359-1/-2 |
| EMS-Grivory Grivory® HT1V-45 HY black 9205 PA6T/6I-GF45 Product description: Grivory HT1V-45 HY black 9205 is a 45% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Grivory HT1V-45 HY .. |
|||
| CTE, linear, Transverse to Flow | 45.0 - 80.0 µm/m-°C | 25.0 - 44.4 µin/in-°F | Average value: 65.5 µm/m-°C Grade Count:10 |
| Overview of materials for Nylon 46, Flame Retarded + Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Flame Retarded + Glass Fiber Reinforced". Each property range of values reported is minimum an.. |
|||
| CTE, linear, Transverse to Flow | 45.0 - 80.0 µm/m-°C | 25.0 - 44.4 µin/in-°F | Average value: 62.8 µm/m-°C Grade Count:18 |
| Overview of materials for Polyphthalamide (PPA), 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are.. |
|||