Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 4.00 mm |
261 °F @Thickness 0.157 in |
Unannealed; ASTM D648 |
LG Chemical Lupoy 1200-15 Polycarbonate Resin Description: LUPOY PC 1200-15 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 4.00 mm |
261 °F @Thickness 0.157 in |
Unannealed; ASTM D648 |
LG Chemical Lupoy 1201-15 Polycarbonate Resin Description: LUPOY PC 1201-15 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 4.00 mm |
261 °F @Thickness 0.157 in |
Unannealed; ASTM D648 |
LG Chemical Lupoy 1201-18 Polycarbonate Resin Description: LUPOY PC 1201-18 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 4.00 mm |
261 °F @Thickness 0.157 in |
Unannealed; ASTM D648 |
LG Chemical Lupoy 1300-15 Polycarbonate Resin Description: LUPOY PC 1300-15 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 4.00 mm |
261 °F @Thickness 0.157 in |
Unannealed; ASTM D648 |
LG Chemical Lupoy 3010-15 Polycarbonate Resin Description: LUPOY PC 3010-15 resin is designed for injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Character.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 4.00 mm |
261 °F @Thickness 0.157 in |
Unannealed; ASTM D648 |
LG Chemical Lupoy 3030-15 Polycarbonate Resin Description: LUPOY PC 3030-15 resin is designed for injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Character.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 4.00 mm |
261 °F @Thickness 0.157 in |
Unannealed; ASTM D648 |
LG Chemical Lupoy 1200HP-15 Polycarbonate Resin Description: LUPOY PC 1200HP-15 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 4.00 mm |
261 °F @Thickness 0.157 in |
Unannealed; ASTM D648 |
LG Chemical Lupoy 1303-15 Polycarbonate Resin Description: LUPOY PC 1303-15 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 4.00 mm |
261 °F @Thickness 0.157 in |
Unannealed; ASTM D648 |
LG Chemical Lupoy 1303AH-15 Polycarbonate Resin Description: LUPOY PC 1303AH-15 Tint Polycarbonate Resin is designed for injection molding of auto-headlamps. It exhibits an excellent physical property balance of heat resistance, transparency and .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR2210 PC LNP* Lubricomp* Lexan_WR2210 compound is an alternative polymeric wear additive technology. No silicones, superior processability/part appearance. Flow similar to LEXAN 121. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 6.40 mm |
261 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR2210 PC LNP* Lubricomp* Lexan_WR2210 compound is an alternative polymeric wear additive technology. No silicones, superior processability/part appearance. Flow similar to LEXAN 121. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR2210 PC (Asia Pacific) Alternative polymeric wear additive technology. No silicones, superior processability/part appearance. Flow similar to LEXAN 121. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 6.40 mm |
261 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR2210 PC (Asia Pacific) Alternative polymeric wear additive technology. No silicones, superior processability/part appearance. Flow similar to LEXAN 121. |