Thermal Properties | Metric | English | Comments |
---|---|---|---|
Glass Transition Temp, Tg | 76.1 - 170 °C | 169 - 338 °F | Average value: 107 °C Grade Count:7 |
Overview of materials for Epoxy/Carbon Fiber Composite This property data is a summary of similar materials in the MatWeb database for the category "Epoxy/Carbon Fiber Composite". Each property range of values reported is minimum and maximum values of a.. |
|||
Glass Transition Temp, Tg | 76.1 °C | 169 °F | Neat Resin; After 24 hr water boil |
Fibre Glast 3100 Style 7781 Prepreg E-Glass Fiberglass Fabric Prepreg fabrics are pre-impregnated with an epoxy resin system. As a result, nearly perfect resin content and maximum, repeatable strength properties are attainable. When properly fabricated, parts .. |
|||
Glass Transition Temp, Tg | 76.1 °C | 169 °F | Neat Resin; After 24 hr water boil |
Fibre Glast 3101 3K, 2x2 Twill Weave Prepreg Carbon Fiber Fabric Prepreg fabrics are pre-impregnated with an epoxy resin system. As a result, nearly perfect resin content and maximum, repeatable strength properties are attainable. When properly fabricated, parts .. |
|||
Glass Transition Temp, Tg | 76.1 °C | 169 °F | Neat Resin; After 24 hr water boil |
Fibre Glast 3102 2x2 Twill Weave Prepreg Kevlar Fabric Prepreg fabrics are pre-impregnated with an epoxy resin system. As a result, nearly perfect resin content and maximum, repeatable strength properties are attainable. When properly fabricated, parts .. |
|||
Glass Transition Temp, Tg | 76.0 °C | 169 °F | |
Lucite International Elvacite ® 2013 Acrylic Resin Elvacite® 2013 is a low molecular weight methyl methacrylate / n-butyl methacrylate copolymer. It is a fast – dissolving, low viscosity grade with quick solvent release for use in industrial.. |
|||
Glass Transition Temp, Tg | 76.0 °C | 169 °F | |
Lucite International Elvacite ® 4402 Acrylic Resin Elvacite® 4402 is a solid methyl methacrylate copolymer bead resin designed for use in formulating environmentally sound thermosetting coatings and adhesives. The resin may be used as the main b.. |
|||
Glass Transition Temp, Tg | 76.0 °C | 169 °F | Ultimate Tg |
Tra-Con Tra-Cast 3108 General Purpose Epoxy Casting Compound TRA-CAST 3108 is a low viscosity two-part formulation recommended for underfill and encapsulating applications where the combination of good mechanical thermal and electrical properties are required.. |
|||
Glass Transition Temp, Tg | 76.0 °C | 169 °F | |
DayGlo Gem-Tone GC-13P Ruby Red Gem-Tone® GC-13P Ruby Red is a rich, strong blue shade red colorant intended for use in clarified polypropylene. Clean, haze free, non-warping color formulations can easily be achieved with the use.. |
|||
Glass Transition Temp, Tg | 76.0 °C | 169 °F | 90 Minute UV Cure; DMA, E" |
3D Systems Accura® SI 40 Plastic for the SLA® 250 System Accura 40 "Ar" or "Hc" type materials - for the SLA 250 system. Mimics Nylon 6:6ApplicationsHigh temperature testing:Under hood bolt-on testingWind tunnel testingHVAC testingPrototyping and testing .. |
|||
Glass Transition Temp, Tg | 75.9 °C | 169 °F | 90 Minute UV Cure; DMA, E" |
3D Systems Accura® SI 40 Plastic for the SLA® 500 System Accura 40 "Ar" or "Hc" type materials - for the SLA 500 system. Mimics Nylon 6:6ApplicationsHigh temperature testing:Under hood bolt-on testingWind tunnel testingHVAC testingPrototyping and testing .. |