Polymer Property : Glass Transition Temp, Tg = 76.1 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Glass Transition Temp, Tg	76.1 - 170 °C	169 - 338 °F	Average value: 107 °C Grade Count:7
Overview of materials for Epoxy/Carbon Fiber Composite This property data is a summary of similar materials in the MatWeb database for the category "Epoxy/Carbon Fiber Composite". Each property range of values reported is minimum and maximum values of a..
Glass Transition Temp, Tg	76.1 Â°C	169 Â°F	Neat Resin; After 24 hr water boil
Fibre Glast 3100 Style 7781 Prepreg E-Glass Fiberglass Fabric Prepreg fabrics are pre-impregnated with an epoxy resin system. As a result, nearly perfect resin content and maximum, repeatable strength properties are attainable. When properly fabricated, parts ..
Glass Transition Temp, Tg	76.1 Â°C	169 Â°F	Neat Resin; After 24 hr water boil
Fibre Glast 3101 3K, 2x2 Twill Weave Prepreg Carbon Fiber Fabric Prepreg fabrics are pre-impregnated with an epoxy resin system. As a result, nearly perfect resin content and maximum, repeatable strength properties are attainable. When properly fabricated, parts ..
Glass Transition Temp, Tg	76.1 Â°C	169 Â°F	Neat Resin; After 24 hr water boil
Fibre Glast 3102 2x2 Twill Weave Prepreg Kevlar Fabric Prepreg fabrics are pre-impregnated with an epoxy resin system. As a result, nearly perfect resin content and maximum, repeatable strength properties are attainable. When properly fabricated, parts ..