Thermal Properties | Metric | English | Comments |
---|---|---|---|
Specific Heat Capacity | 0.595 J/g-°C @Temperature 800 °C |
0.142 BTU/lb-°F @Temperature 1470 °F |
|
Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 800 °C |
0.142 BTU/lb-°F @Temperature 1470 °F |
|
Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 800 °C |
0.142 BTU/lb-°F @Temperature 1470 °F |
|
Haynes 230® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 800 °C |
0.142 BTU/lb-°F @Temperature 1470 °F |
|
Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 800 °C |
0.142 BTU/lb-°F @Temperature 1470 °F |
|
Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 800 °C |
0.142 BTU/lb-°F @Temperature 1470 °F |
|
Haynes 230® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 800 °C |
0.142 BTU/lb-°F @Temperature 1470 °F |
|
Haynes 230® alloy, 30% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 800 °C |
0.142 BTU/lb-°F @Temperature 1470 °F |
|
Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 800 °C |
0.142 BTU/lb-°F @Temperature 1470 °F |
|
Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 800 °C |
0.142 BTU/lb-°F @Temperature 1470 °F |
|
Haynes 230® alloy, plate, 4000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 800 °C |
0.142 BTU/lb-°F @Temperature 1470 °F |
|
Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 700 °C |
0.142 BTU/lb-°F @Temperature 1290 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 900 °C |
0.142 BTU/lb-°F @Temperature 1650 °F |
|
Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 900 °C |
0.142 BTU/lb-°F @Temperature 1650 °F |
|
Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 900 °C |
0.142 BTU/lb-°F @Temperature 1650 °F |
|
Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 900 °C |
0.142 BTU/lb-°F @Temperature 1650 °F |
|
Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 900 °C |
0.142 BTU/lb-°F @Temperature 1650 °F |
|
Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 900 °C |
0.142 BTU/lb-°F @Temperature 1650 °F |
|
Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 900 °C |
0.142 BTU/lb-°F @Temperature 1650 °F |
|
Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 900 °C |
0.142 BTU/lb-°F @Temperature 1650 °F |
|
Haynes 556® alloy, bar, after 8000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 900 °C |
0.142 BTU/lb-°F @Temperature 1650 °F |
|
Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 900 °C |
0.142 BTU/lb-°F @Temperature 1650 °F |
|
Haynes 556® alloy, hot rolled, solution annealed plate, 6.4-12.7 mm (1/2 in.) thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 700 °C |
0.142 BTU/lb-°F @Temperature 1290 °F |
|
Haynes Hastelloy® B-3® alloy, 50% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Specific Heat Capacity | 0.595 J/g-°C | 0.142 BTU/lb-°F | |
Schott N-SK2 Glass Information Provided by SCHOTT North America, Inc. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 800 °C |
0.142 BTU/lb-°F @Temperature 1470 °F |
|
Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 800 °C |
0.142 BTU/lb-°F @Temperature 1470 °F |
|
Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 900 °C |
0.142 BTU/lb-°F @Temperature 1650 °F |
|
Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 800 °C |
0.142 BTU/lb-°F @Temperature 1470 °F |
|
Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 900 °C |
0.142 BTU/lb-°F @Temperature 1650 °F |
|
Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Specific Heat Capacity | 0.595 J/g-°C @Temperature 900 °C |
0.142 BTU/lb-°F @Temperature 1650 °F |
|
Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |