- Polymer Property : Specific Heat Capacity = 0.106 BTU/lb-°F
Polymer Property : Specific Heat Capacity = 0.106 BTU/lb-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, hot rolled and 1175°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C @Temperature 200 °C |
0.106 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C | 0.106 BTU/lb-°F | |
| Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 3 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness Tensile and bearing strengths (ultimate and yield) and elongation values reported here are typical for Cold Rolled Sheet, 3 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness samples. Density and m.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C | 0.106 BTU/lb-°F | |
| Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, Solution Treated Tensile strength (ultimate and yield), and elongation values reported here are typical for Cold Rolled Sheet, Solution Treated samples. Density and magnetic permeability are typical of annealed INCO.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C | 0.106 BTU/lb-°F | |
| Special Metals INCONEL® 706 Precipitation Hardening Alloy, Forged Disc, 2 Part Heat Treatment Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, 2 Part Heat Treatment samples. Density and magnetic permeability are typica.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C | 0.106 BTU/lb-°F | |
| Special Metals INCONEL® 706 Precipitation Hardening Alloy, Forged Disc, Solution Treated Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, Solution Treated samples. Density and magnetic permeability are typical of .. |
|||
| Specific Heat Capacity | 0.444 J/g-°C | 0.106 BTU/lb-°F | |
| Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Flat, 2 Part Heat Treatment, 1.250 inch (31.8 mm) Thickness Tensile strength (ultimate and yield), shear strength, compressive strength, reduction of area, and elongation values reported here are typical for Hot Finished Flat, 2 Part Heat Treatment, 1.250 in.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C | 0.106 BTU/lb-°F | |
| Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diameter Tensile strength (ultimate and yield), compressive strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diamete.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C | 0.106 BTU/lb-°F | |
| Special Metals INCONEL® Alloy 600 A nickel-chromium alloy with good oxidation resistance at high temperatures and resistance to chloride-ion stress-corrosion cracking, corrosion by high-purity water, and caustic corrosion. Used for.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C | 0.106 BTU/lb-°F | |
| Special Metals NIMONIC® Alloy 115 A precipitation-hardenable nickel-chromium-cobalt alloy with an addition of molybdenum for solid-solution strengthening. It is similar to NIMONIC alloy 105 but has higher levels of aluminum and tit.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C | 0.106 BTU/lb-°F | |
| Carlson C 600 Nickel-Chromium-Iron Alloy Carlson Alloy C 600 is nickel-chromium alloy, developed for use in severely corrosive environments at elevated temperatures. The high nickel content of this alloy provides excellent resistance to c.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C | 0.106 BTU/lb-°F | |
| Carlson C 600ESR Nickel-Chromium-Iron Alloy General DescriptionCarlson Alloy C 600 is nickel-chromium alloy, developed for use in severely corrosive environments at elevated temperatures. The high nickel content of this alloy provides excell.. |
|||
| Specific Heat Capacity | 0.442 J/g-°C @Temperature 50.0 °C |
0.106 BTU/lb-°F @Temperature 122 °F |
|
| Special Metals INCOLOY® Alloy 903 A nickel-iron-cobalt alloy with additions of niobium, titanium, and aluminum for precipitation hardening. The alloy combines high strength with a low and constant coefficient of thermal expansion a.. |
|||
| Specific Heat Capacity | 0.444 J/g-°C | 0.106 BTU/lb-°F | |
| Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 2 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness Tensile and bearing strengths (ultimate and yield) and elongation values reported here are typical for Cold Rolled Sheet, 2 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness samples. Density and m.. |
|||