Thermal Properties | Metric | English | Comments |
---|---|---|---|
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Specific Heat Capacity | 0.427 J/g-°C | 0.102 BTU/lb-°F | |
HP Alloys Alloy C-276, 10% Cold Worked 10% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
Specific Heat Capacity | 0.427 J/g-°C | 0.102 BTU/lb-°F | |
HP Alloys Alloy C-276, 20% Cold Worked 20% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
Specific Heat Capacity | 0.427 J/g-°C | 0.102 BTU/lb-°F | |
HP Alloys Alloy C-276, 50% Cold Worked 50% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
Specific Heat Capacity | 0.427 J/g-°C | 0.102 BTU/lb-°F | |
Special Metals INCOLOY® Alloy 909 A nickel-iron-cobalt alloy with a silicon addition and containing niobium and titanium for precipitation hardening. It is similar to INCOLOY alloys 903 and 907 in that it has low thermal expansion .. |
|||
Specific Heat Capacity | 0.427 J/g-°C | 0.102 BTU/lb-°F | |
Special Metals INCONEL® Alloy C-276 A nickel-molybdenum-chromium alloy with an addition of tungsten having excellent corrosion resistance in a wide range of severe environments. The high molybdenum content makes the alloy especially .. |
|||
Specific Heat Capacity | 0.427 J/g-°C | 0.102 BTU/lb-°F | |
Special Metals INCONEL® C276 Nickel Superalloy Plate Tensile strength (ultimate and yield) and elongation values reported here are typical for annealed plate. Other property values are typical of INCO® C276.Data provided by the manufacturer, Specia.. |
|||
Specific Heat Capacity | 0.427 J/g-°C | 0.102 BTU/lb-°F | |
Special Metals INCONEL® C276 Nickel Superalloy Tubing, 0% Cold Work (Annealed) Tensile strength (ultimate and yield) and elongation values reported here are typical for annealed tubing. Other property values are typical of INCO® C276.Data provided by the manufacturer, Speci.. |
|||
Specific Heat Capacity | 0.427 J/g-°C | 0.102 BTU/lb-°F | |
Special Metals INCONEL® C276 Nickel Superalloy Tubing, 24% Cold Work Tensile strength (ultimate and yield) and elongation values reported here are typical for annealed + 24% cold worked tubing. Other property values are typical of INCO® C276.Data provided by the m.. |
|||
Specific Heat Capacity | 0.427 J/g-°C | 0.102 BTU/lb-°F | |
Special Metals INCONEL® C276 Nickel Superalloy Tubing, 30% Cold Work Tensile strength (ultimate and yield) and elongation values reported here are typical for annealed + 30% cold worked tubing. Other property values are typical of INCO® C276.Data provided by the m.. |
|||
Specific Heat Capacity | 0.427 J/g-°C | 0.102 BTU/lb-°F | |
Special Metals MONEL® Alloy R-405 The free-machining version of MONEL alloy 400. A controlled amount of sulfur is added to the alloy to provide sulfide inclusions that act as chip breakers during machining. Other characteristics a.. |
|||
Specific Heat Capacity | 0.427 J/g-°C | 0.102 BTU/lb-°F | |
Carlson GOC 276 Nickel-Molybdenum-Chromium General DescriptionCarlson Alloy GOC 276 is a nickel-molybdenum-chromium alloy exhibiting outstanding corrosion resistance over a wide range of service environments. This alloy is generally use in .. |
|||
Specific Heat Capacity | 0.427 J/g-°C @Temperature 0.000 - 100 °C |
0.102 BTU/lb-°F @Temperature 32.0 - 212 °F |
|
AK Steel 444 Ferritic Stainless steel AK Steel 444 is a low-carbon, low nitrogen, ferritic stainless steel that provides pitting and crevice corrosion resistance superior to most ferritic stainless steels. Applications requiring superi.. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Specific Heat Capacity | 0.428 J/g-°C @Temperature 100 °C |
0.102 BTU/lb-°F @Temperature 212 °F |
|
Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |