Thermal Properties | Metric | English | Comments |
---|---|---|---|
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, plate, 4000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, plate, 8000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 200 °C |
0.100 BTU/lb-°F @Temperature 392 °F |
|
Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 200 °C |
0.100 BTU/lb-°F @Temperature 392 °F |
|
Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 200 °C |
0.100 BTU/lb-°F @Temperature 392 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 200 °C |
0.100 BTU/lb-°F @Temperature 392 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Specific Heat Capacity | 0.419 J/g-°C | 0.100 BTU/lb-°F | |
Special Metals INCOLOY® A-286 Iron-Nickel-Chromium Alloy Data provided by the manufacturer, Special Metals. |
|||
Specific Heat Capacity | 0.418 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Schmolz + Bickenbach MoldMAX HH® High Hard - Copper Alloy Description: Brush Wellman’s MoldMAX HH® (High Hard) is the premier copper mold alloy. This alloy has a hardness and strength comparable with standard tool steels but its thermal conductivit.. |
|||
Specific Heat Capacity | 0.418 J/g-°C | 0.100 BTU/lb-°F | |
Weartech International WT-60 Nickel Hardfacing & Wear Resistant Alloy Applications: pump sleevesInformation provided by Weartech International |
|||
Specific Heat Capacity | 0.420 J/g-°C | 0.100 BTU/lb-°F | |
CLAL-MSX NICLAL 1800 0 Annealed Copper Alloy, Free Cutting Nickel-Silver Main Characteristics: Good corrosion resistanceHigh mechanical propertiesTypical Applications:Parts subject to high stressHigh quality fastenersInformation provided by CLAL-MSX |
|||
Specific Heat Capacity | 0.418 J/g-°C | 0.100 BTU/lb-°F | |
Bohler-Uddeholm BÖHLER S390 MICROCLEAN® High Speed Steel Description: High speed steel produced by powder-metallurgy methods with highest red hardness, compressive strength and wear resistance. The PM technology imparts to the material also excellent toug.. |
|||
Specific Heat Capacity | 0.418 J/g-°C @Temperature 20.0 °C |
0.100 BTU/lb-°F @Temperature 68.0 °F |
|
Carlson 2205 (UNS S31803) Duplex Stainless Steel General DescriptionCarlson Alloy 2205 is a second-generation, nitrogen-alloyed duplex stainless steel (ferritic-austenitic). It offers an excellent combination of both strength and corrosion resist.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 0.000 - 100 °C |
0.100 BTU/lb-°F @Temperature 32.0 - 212 °F |
condition H 900 |
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1150M (Heated 760°C/2hr/AC then 621°C/4hr/AC) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
Specific Heat Capacity | 0.420 J/g-°C | 0.100 BTU/lb-°F | |
ATI Allegheny Ludlum AL 2205™ Duplex Stainless Steel, Sheet and Strip < 0.1875", UNS S31803 Ferromagnetic. The AL 2205 alloy is a nitrogen-enhanced duplex stainless steel alloy. The nitrogen serves to significantly improved the corrosion resistance of the alloy; especially in the welded c.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 0.000 - 100 °C |
0.100 BTU/lb-°F @Temperature 32.0 - 212 °F |
condition H 900 |
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 1025 (Heated 552°C) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio.. |
|||
Specific Heat Capacity | 0.419 J/g-°C @Temperature 100 °C |
0.100 BTU/lb-°F @Temperature 212 °F |
|
Haynes 230® alloy, 50% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |