Thermal Properties | Metric | English | Comments |
---|---|---|---|
Clash Berg Stiffness Temperature | -26.0 °C | -14.8 °F | T-10000 Torsional stiffness ASTM D1043-72(1981) |
DuPont Performance Polymers Hypalon® HPG-6525 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound
&n Carbon black compound with 100 parts Hypalon; 27.8 parts sublimed litharge dispersion; 55 parts carbon black; 55 parts aromatic process oil; 0.5 parts MTBS; and 2 parts Tetrone® A rubber accelerato.. |
|||
Clash Berg Stiffness Temperature | -26.0 °C | -14.8 °F | At 69 MPa |
DuPont Vamac® G Sample Compound Vulcanizate Slab Cure (10 minutes at 177°C) Vulcanizate performance test data can help end-users evaluate the potential fitness of similar compounds for their own applications.Information provided by DuPont. |
|||
Clash Berg Stiffness Temperature | -26.0 °C | -14.8 °F | T-10000 Torsional stiffness ASTM D1043-72(1981) |
DuPont Performance Polymers Hypalon® 4085 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound
(disc Mineral filled compound with 100 parts Hypalon; 80 parts hard clay; 4 parts magnesia; 30 parts aromatic process oil; 3 parts pentaerythritol; and 2 parts Tetrone® A rubber accelerator (from DuPont .. |
|||
Clash Berg Stiffness Temperature | -26.0 - 7.00 °C | -14.8 - 44.6 °F | Average value: -17.6 °C Grade Count:15 |
Overview of materials for Chlorosulfonated Polyethylene Rubber This property data is a summary of similar materials in the MatWeb database for the category "Chlorosulfonated Polyethylene Rubber". Each property range of values reported is minimum and maximum val.. |