- Polymer Property : CTE, linear, Parallel to Flow = 42.0 µm/m-°C
Polymer Property : CTE, linear, Parallel to Flow = 42.0 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP LUBRICOMP KFI16 Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KFI16 is a compound based on Acetal Copolymer resin containing Glass Fiber, Silicone. |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| SABIC Innovative Plastics NORYL ZM3640 PPE+PS (Asia Pacific) |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP LUBRICOMP RFL22E PA6.6 (Europe-Africa-Middle East) LNP* LUBRICOMP* RFL22E Is a compound based on PA66 resin, containing Glass Fiber and PTFE. Added features include: Internally Lubricated, Easy Moulding |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP LUBRICOMP RFL369 PA6.6 (Europe-Africa-Middle East) LNP* LUBRICOMP* RFL369 is a compound based on PA 66 resin containing Glass Fiber, PTFE, Flame Retardant. Added features include: Flame Retardant, internally lubricated |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP LUBRICOMP RX94033 PA6.6 (Europe-Africa-Middle East) LNP* LUBRICOMP* RX94033 is a compound based on PA 66 resin containing Aramide Fiber, Glass Fiber, PTFE. Added features include: Internally Lubricated. |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP STAT-KON DC10EPFR PC LNP* STAT-KON* Lexan_DC10EPFR is a compound based on Polycarbonate containing Carbon Fiber. Added features of this grade include: Exceptional Processing, Flame Retardant, Electrically Conductive. |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP THERMOCOMP JF003E PES LNP* THERMOCOMP* JF003E is a compound based on Polyethersulfone resin containing 15% Glass Fiber. Added features of this material include: Easy Molding. |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP THERMOCOMP KF008 Acetal Copolymer (Europe-Africa-Middle East) LNP* THERMOCOMP* KF008 is a compound based on Acetal Copolymer resin containing Glass Fiber. |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP Thermocomp PFB139E PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PFB139E is a compound based on PA 6 resin containing Glass Fiber, Glass Bead, Flame Retardant. Added features include; Flame Retardant, Easy Molding.This data was supplied by SABIC-.. |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP THERMOCOMP RF003ES PA 66 LNP* THERMOCOMP* RF003ES is a Nylon 66 base resin containing 15% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP THERMOCOMP RX08401 PA 66 LNP* Thermocomp* RX08401 is a compound based on Nylon 66 containing Glass Fiber. Added feature of this grade include: Impact Modified. |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| SABIC Innovative Plastics LNP THERMOCOMP RX10408H PA 66 LNP* Thermocomp* RX10408H is a compound based on Nylon 66 containing Proprietary Fillers. Characteristics are: Radiopacity and Healthcare. |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| SABIC Innovative Plastics LNP Thermocomp ZF008 PPO LNP* Thermocomp* ZF008 is a compound based on Modified PPO containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| SABIC Innovative Plastics LNP Thermocomp RFB53U PA 66 (Europe-Africa-Middle East) LNP*THERMOCOMP*RFB53U is a compound based on PA 66 resin containing Glass Bead, Glass Fiber. Added features include: UV-Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle E.. |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C | 23.3 µin/in-°F | ISO 11359-1/-2 |
| Covestro Bayblend® T88-2N Polycarbonate + ABS, 10% Glass Filled Injection molding grade10 % glass fiber filledtensile modulus = 3900 MPaVicat/B 120 temperature = 131 °CPreprocessingMax. Water content |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 20.0 °C |
23.3 µin/in-°F @Temperature 68.0 °F |
|
| Covestro Baygal® 90 IK 69 Polyurethane Uses: Suitable for impregnation and encapsulation of coils, especially when high heat deflection temperature, and eventually fire resistance is requested.Information provided by Bayer.As of 1 Septem.. |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Eurostar Staramide RFB53U PA66, 50% Glass Bead/Fiber Filled, Injection Molded RFB53U is a Glass Bead/ Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as Staramide 66 1525 VK Z4)Information provided by Eurostar. |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 20.0 °C |
23.3 µin/in-°F @Temperature 68.0 °F |
|
| Covestro Bayblend® T 88-2N Polycarbonate/ABS Blend, 10% Glass Fiber Contains 10% glass fiber reinforcement, high stiffness.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – .. |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C | 23.3 µin/in-°F | dry; ISO 11359-1/-2 |
| DSM EcoPaXX® Q-HG10 PA410-GF50 50% Glass Reinforced, Heat Stabilized |
|||
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Eurostar Starflam PFB139E PA6, Glass Fiber/Bead Filled, Flame Retardant, Injection Molded Starflam PFB139E is a Flame Retardant Glass Bead and Glass Fiber Reinforced Polyamide 6 Injection Molding Resin (also known as PFB1013Z590)Information provided by Eurostar. |
|||