Thermal Properties | Metric | English | Comments |
---|---|---|---|
Vicat Softening Point | 248 °C | 478 °F | B/50; ISO R306 |
Samsung Cheil Industries Infino® HT-8200G MPPE/PA, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Vicat Softening Point | 248 °C | 478 °F | B/50; ISO R306 |
Samsung Cheil Industries Infino® HT-8200G MPPE/PA, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Vicat Softening Point | 248 °C | 478 °F | B/120; ISO 306 |
Sax Polymers SAXAMID 226F4RY01 Nylon 6.6, 20% Glass Fiber SAXAMID 226F4RY01 is a polyamide 6.6 injection-molding-grade reinforced with 20% glass fibers. It has a halogen-free flame retardant.Information provided by SAX Polymers |
|||
Vicat Softening Point | 248 °C | 478 °F | B/120; ISO 306 |
Sax Polymers SAXAMID 226F5RY01 Nylon 6.6, 25% Glass Fiber SAXAMID 226F5RY01 is a polyamide 6.6 injection-molding-grade reinforced with 25% glass fibers. It has a halogen-free flame retardant and UL listed.Information provided by SAX Polymers |
|||
Vicat Softening Point | 248 °C | 478 °F | Rate B/50; ASTM D1525 |
SABIC Innovative Plastics NORYL GTX GTX820 PPE+PS+PA GR 20%. Higher stiffness of 800000 psi (4000 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: valves. |
|||
Vicat Softening Point | 248 °C | 478 °F | Rate B/50; ASTM D1525 |
SABIC Innovative Plastics NORYL GTX GTX820 PPE+PS+PA (Asia Pacific) GR 20%. Higher stiffness of 800000 psi (4000 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: valves. |
|||
Vicat Softening Point | 248 °C | 478 °F | Rate B/50; ASTM D1525 |
SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA 30% Glass Reinforced PPE+PA Alloy. |
|||
Vicat Softening Point | 248 °C | 478 °F | Rate B/50; ASTM D1525 |
SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA (Asia Pacific) GR 30%. Highest stiffness of 1200000 psi (8200 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: under the bonnet. |