Thermal Properties | Metric | English | Comments |
---|---|---|---|
Vicat Softening Point | 63.9 °C | 147 °F | ASTM D1525 |
ExxonMobil OPTEMA™ TC 115 Blown Film Resin
(discontinued **) OPTEMA TC 115 is an ethylene methyl acrylate copolymer, designed for specialty blown film applications. It yields soft, elastic films.Information provided by ExxonMobil Chemical |
|||
Vicat Softening Point | 64.0 °C | 147 °F | ASTM D1525 |
DuPont Bynel® E403 Acid-Modified Ethylene Terpolymer Adhesive Resin
(discontinued **) Bynel® Series 2000 resins are acid-modified ethylene terpolymers with medium to high acid comonomer contents. They contain a temperature stable ester that makes them functional in high-temperature .. |
|||
Vicat Softening Point | 64.0 °C | 147 °F | ASTM D1525 |
DuPont Appeel® LSR 11D569 Modified EVA Lidding Sealing Resin
(discontinued **) Appeel 11D569 is a modified ethylene vinyl acetate copolymer resin designed to be used as a sealing layer for lidding applications. It provides peelable seals to a variety of surfaces including poly.. |
|||
Vicat Softening Point | 64.0 °C | 147 °F | 1000g; ASTM D-1525 |
ExxonMobil Escorene® LD-720 High EVA Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A high vinyl acetate copolymer specialty film resin designed for applications requiring outstanding heat sealability along with excellent strength p.. |
|||
Vicat Softening Point | 64.0 - 178 °C | 147 - 352 °F | Average value: 117 °C Grade Count:9 |
Overview of materials for Cyclo Olefin Polymer This property data is a summary of similar materials in the MatWeb database for the category "Cyclo Olefin Polymer". Each property range of values reported is minimum and maximum values of appropria.. |
|||
Vicat Softening Point | 64.0 °C | 147 °F | ASTM D1525 |
DuPont™ Surlyn® 1605SBR Sodium Ionomer Resin for Extrusion Coating
(discontinued **) Surlyn® 1605SBR is an ionomer resin available for use in conventional extrusion coating and coextrusion coating equipment designed to process polyethylene resins. Applications: Medical/pharmaceuti.. |
|||
Vicat Softening Point | 64.0 °C | 147 °F | ISO 306 |
Iran Petrochemical (PCC) I2 HB 7250 High Density Polyethylene I2 (HB 7250) is a high density polyethylene with Propylene as comonomer. It is easy flowing, low warpage, less hard and stiff than I1.Applications: household articles, closures/seals, packaging.Info.. |
|||
Vicat Softening Point | 64.0 °C | 147 °F | 50°C/h; 50N; 10x10x4mm; ISO 306/B50 |
SYNTHOS Krasten® FB28 High Impact Polystyrene And Polyethylene Blend Polymer blend HIPS/PE. High toughness, very good tensile properties and environmental stress cracking resistance. Processed mainly by extrusion and thermoforming. Production of sheets and films, tec.. |
|||
Vicat Softening Point | 64.0 °C | 147 °F | ASTM D1525 |
DuPont Elvax® 460 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Vicat Softening Point | 64.0 °C | 147 °F | ISO 306 |
Total EVA 1020 VN 5 Ethylene Vinyl Acetate Copolymer - Blown Film EVA 1020 VN 5 is made by a high pressure tubular process. Grade for very flexible films with very high transparency and good mechanical properties. Contains an antioxidant.Application examples: Ch.. |
|||
Vicat Softening Point | 64.0 °C | 147 °F | ASTM D1525 |
DuPont Elvax® 550 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Vicat Softening Point | 64.0 °C | 147 °F | VST/A50; ISO 306 |
Topas Advanced Polymers TOPAS® Elastomer E-140 Developmental Cyclic Olefin Copolymer (COC) TOPAS® Elastomer E-140, unlike most TOPAS grades, is a semicrystalline cyclic olefin material with flexibility. It is a fairly stiff elastomer which can be extruded and injection molded, and can be.. |
|||
Vicat Softening Point | 63.9 °C | 147 °F | ASTM D1525 |
ExxonMobil Escorene® LD 713.93 Cast Film Resin Escorene Ultra LD 713.93 is a 14.4 wt% vinyl acetate copolymer film resin. Film made from LD 713.93 exhbits very high impact strength, hihg clarity, and excellent heat sealabilityAvailability: Latin.. |
|||
Vicat Softening Point | 64.0 °C | 147 °F | ASTM D1525 |
DuPont™ Surlyn® 1605 Sodium Ionomer Resin for Blown/Cast Film and Extrusion Coating Surlyn® 1605 is an ionomer resin available for use in conventional blown and cast film extrusion and coextrusion equipment and extrusion coating and coextrusion coating equipment designed to proces.. |
|||
Vicat Softening Point | 64.0 °C | 147 °F | |
BASF Novolen® 2309 L Polypropylene Cast film and thermoformed partsData was collected by ISO methods and provided by BASF. |
|||
Vicat Softening Point | 63.9 °C | 147 °F | ASTM D1525 |
ExxonMobil Escorene® LD 728.61 Molding, extrusion and compounding resin Escorene Ultra LD 728.61 is a high vinyl acetate copolymer with low melting temperature and excellent strength properties and toughness.Availability: Latin America, North America and South America A.. |
|||
Vicat Softening Point | 64.0 °C @Load 1.02 kg |
147 °F @Load 2.25 lb |
ASTM D1525 |
Arkema Group LOTRYL® 16 MA 003 Copolymer Ethylene - Methyl Acrylate LOTRYL® 16 MA 003 is a random copolymer of ethylene and methyl acrylate made by high-pressure radicalar polymerisation process. Due to the methyl acrylate content, LOTRYL® 16 MA 003 is a polymer o.. |