Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 250 MPa @Temperature 23.0 °C |
36300 psi @Temperature 73.4 °F |
ISO 178 |
Victrex® PEEK 150GL20 Polyetheretherketone, 20% Glass Fibre Reinforced Product Description:High performance thermoplastic material, 20% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food conta.. |
|||
Flexural Strength | 250 MPa @Temperature 23.0 °C |
36300 psi @Temperature 73.4 °F |
ISO 178 |
Victrex® PEEK 450GL30 Polyetheretherketone, 30% Glass Fiber, Black Product Description: High performance thermoplastic material, 30% glass fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, Standard viscos.. |
|||
Flexural Strength | 250 MPa @Temperature 125 °C |
36300 psi @Temperature 257 °F |
ISO 178 |
Victrex® PEEK 650CA30 30% Carbon Fiber Filled, PolyEtherEtherKetone High performance thermoplastic material, 30% carbon fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and extrusion, low flow, FDA food contact compliant.. |
|||
Flexural Strength | 250 MPa @Strain 3.00 % |
36300 psi @Strain 3.00 % |
d.a.m., 2 mm/min; ISO 178-A |
Lanxess Durethan® AM 40 X H2.0 901510 Nylon 66, Glass Fiber/Mineral Reinforced PA 66, 40% glass fibers/mineral, injection molding, heat-aging stabilized, low tendency to warpInformation provided by LANXESS. |
|||
Flexural Strength | 250 MPa @Strain 4.30 % |
36300 psi @Strain 4.30 % |
d.a.m., 2 mm/min; ISO 178-A |
Lanxess Durethan® BKV 130 H2.0 DUS008 901510 Nylon 6, Glass Fiber Reinforced, Impact Modified PA 6, 30% glass fibers, injection molding, impact modified, heat-aging stabilizedInformation provided by LANXESS. |
|||
Flexural Strength | 250 MPa @Strain 3.70 % |
36300 psi @Strain 3.70 % |
d.a.m., 2 mm/min; ISO 178-A |
Lanxess Durethan® DP BKV 35 XF 901510 Nylon 6, 35% Glass Fiber PA 6, 35% glass fibers, injection molding, improved flowability, improved surface finishInformation provided by LANXESS. |
|||
Flexural Strength | 250 MPa @Temperature -40.0 °C |
36300 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.7%); ASTM-D790 |
Toyobo GLAMIDE® T-602G30 MXD66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
Flexural Strength | 250 MPa @Temperature -40.0 °C |
36300 psi @Temperature -40.0 °F |
Practical Use; ASTM-D790 |
Toyobo GLAMIDE® T-669VGB Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
Flexural Strength | 250 MPa @Temperature 23.0 °C |
36300 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 |
Toyobo GLAMIDE® TY-791HT 6T-Nylon GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
Flexural Strength | 250 MPa @Thickness >=20.0 mm |
36300 psi @Thickness >=0.787 in |
ISO 178; IEC/EN 60893-2 5.1 |
Elektro-Isola G-Etronax PM H Polyester, Glass Mat, Creme, Sheets Description: A reasonably-priced alternative to other high-temperature types. Low thermal conductivity. Applications: Used as, among other things, thermal insulation plates where high strength prope.. |
|||
Flexural Strength | 250 MPa @Thickness >=1.50 mm |
36300 psi @Thickness >=0.0591 in |
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1 |
Elektro-Isola G-Etronax PM H Polyester, Glass Mat, Creme, Sheets Description: A reasonably-priced alternative to other high-temperature types. Low thermal conductivity. Applications: Used as, among other things, thermal insulation plates where high strength prope.. |
|||
Flexural Strength | 250 MPa @Thickness >=1.50 mm |
36300 psi @Thickness >=0.0591 in |
1hr/130°C/measured at 130°C; ISO 178; IEC/EN 60893-2 5.1 |
Elektro-Isola G-Etronax EP 10 Epoxy, Glass Fabric Reinforcement, Light Yellow, Sheets Description: High mechanical strength at elevated temperatures. Very good stability of electrical properties under high humidity. Mechanical, electrical and electronic applications. Can be used at c.. |