Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 89.6 MPa @Temperature 232 °C |
13000 psi @Temperature 450 °F |
ASTM D790 |
Solvay Specialty Polymers Torlon® 4435 Polyamide-imide (PAI)
(Unverified Data**) Torlon 4435 is a polyamide-imide resin specifically designed to provide exceptionally low wear performance in non-lubricated applications even at high pressure and velocity (PV) conditions. Not only.. |
|||
Flexural Strength | 89.6 MPa @Thickness 1.57 mm |
13000 psi @Thickness 0.0620 in |
CW; ASTM D790 |
Industrial Laminates/Norplex NP193M Synthetic Fabric Base Grade Description: 17 oz. aramide and “soft glass†fibers are combined to make a fabric that is stronger than pure aramide and less abrasive than glass fabrics. This material is impregnated with.. |
|||
Flexural Strength | 89.6 MPa @Thickness 1.57 mm |
13000 psi @Thickness 0.0620 in |
CW; ASTM D790 |
Industrial Laminates/Norplex NP691 Paper Base Laminate Description: Flame resistant, room temperature punching grade. NP691 is very similar to NP612 in electrical properties and mechanical strength, with improved moisture resistance.Thickness Tested: 0... |
|||
Flexural Strength | 89.6 MPa @Temperature 232 °C |
13000 psi @Temperature 450 °F |
ASTM D790 |
Solvay Specialty Polymers Torlon® 4435 Polyamide-imide (PAI) Torlon® 4435 is a polyamide-imide resin specifically designed to provide exceptionally low wear performance in non-lubricated applications even at high pressure and velocity (PV) conditions. Not .. |
|||
Flexural Strength | 89.6 MPa @Temperature 23.9 °C |
13000 psi @Temperature 75.0 °F |
ASTM D790 |
Saint-Gobain Meldin® 7022 CM Compression Molded Graphite Filled Polyimide Melidin® 7022 CM is a compression molded polyimide that contains 40% graphite filler. This grade offers additional dimensional stability at elevated temperatures and the lowest CTE of any Meldin.. |