Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 6.70 GPa | 972 ksi | ISO 178 |
Radici Radilon® SERV3808 K (dry) Nylon 6 Heat stabilized glass-fiber reinforced with high impact strengthInformation provided by Radici group. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | ASTM-D790 |
Polyram PE322G22 PET, 22% Glass Fiber
(discontinued **) 22% Glass fiber reinforced, flame retardant PET for injection molding applications.Information provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DCP32 PC LNP* Lubricomp* DCP32 is a compound based on Polycarbonate resin containing 15% PTFE/Silicone, 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubrica.. |
|||
Flexural Modulus | 6.70 - 19.0 GPa | 972 - 2760 ksi | Average value: 8.15 GPa Grade Count:19 |
Overview of materials for Phenolic, Novolac, Impact Grade, Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Impact Grade, Filled". Each property range of values reported is minimum and maximum .. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | |
Idemitsu Kosan Xarec® N WA 7020 SPS, 20% Glass Filled Crystalline Polymer Blend, Glass Filled, Impact Modified. Used in Automotive Electronics applications. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | ISO 178 |
Idemitsu Kosan Xarec® WA 204 SPS, 20% Glass Filled Crystalline Polymer, Glass Filled, Impact Modified. Used in Automotive and Industrial applications. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | cond., 2 mm/min; ISO 178-A |
Lanxess Durethan® AKV 35 H2.0 SR1 901510 Nylon 66, Glass Fiber Reinforced PA 66, 35% glass fibers, injection molding, heat-aging stabilized, improved surface finishInformation provided by LANXESS. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RX01075 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RX01075 is a compound based on Nylon 66 resin containing PTFE, Mineral. Added features of this material include: Heat Stabilized. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | ASTM D790 |
Plenco 2567 Phenolic, Granular, Injection Molded PLENCO 02567 is a general purpose, organic filled phenolic molding compound offering excellent cosmetic characteristics as typically required for vacuum metalized closures. UL recognized under compo.. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | ISO 178 |
Unitika BV2120G15 PA66, 15% Glass Fiber Reinforced, Flame Retardant, Dry Information provided by Unitika Ltd. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | ASTM D790 |
Plenco 7021 Phenolic, Granular, Injection Molded PLENCO 07021 is a renumber of Plaslok 7021 which is the replacement material for the former Union Carbide BMRS-7021. It is a two-stage, impact grade phenolic molding compound suitable for compressio.. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | ASTM D790 |
Plenco 7200 Phenolic, Granular, Transfer Molded PLENCO 07200 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength, good powder properties and excellent cosmetic properties. UL recognized under component .. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | ASTM-D790 |
Polyram PlusTek PA320G5 Nylon 6.6, 25% Glass Fiber, Flame Retardant 25% glass fiber reinforced, flame retardant and high stiffness polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | ISO 178 |
Wellman EcoLon® MRGF1518-BK Mineral/Glass Fiber Reinforced Nylon 66, Lubricated, Heat Stabilized, PCR Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co.. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | ISO 178 |
Polyram Polytron P40N11 Polypropylene, 40% Long Glass Fibers A chemically coupled 40% long glass fiber reinforced natural polypropylene, heat stabilized, for injection molding applications.Information provided by Polyram. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6000 MX 400 CP Combination Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | 2 mm/min; ISO 178 |
Eurostar Starflam RF0052E PA66/6, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam RF0052E is a Flame Retardant, Halogen Free, Red Phosphorous Free, Glass Reinforced Polyamide 66/6 Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | ASTM D790 |
Ashley Polymers Ashlene® 630-25G Nylon 6, 25% Glass Reinforced Nylon 6, 25% glass reinforced resin.Data provided by the manufacturer |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | ASTM D790 |
Ashley Polymers Ashlene® 630-30G Nylon 6, 30% Glass Reinforced Nylon 6, 30% glass reinforced resin.Data provided by the manufacturer |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | ISO 178 |
BASF Ultramid® B3ZG8 BK 20560 40% Glass Filled PA6-1 (Conditioned) Description: Impact-modified and 40% glass-fiber reinforced injection-molding grade for technical articles of very high stiffness and toughness, for instance, for vehicle airbag housings and suitcas.. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DCP32 PC (Asia Pacific) LNP* Lubricomp* DCP32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Electrically Conductive, Internally Lubricated. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | ASTM D790 |
E-Polymers TEKAMID® TB120GM40 , 40% GF/MF Reinforced PA6, DAM 40% GF/MF reinforced, Good surface, Low warpageInformation provided by E-Polymers Co. Ltd. |
|||
Flexural Modulus | 6.70 GPa | 972 ksi | |
Plastcom SLOVASTER® B1 GF 30 PBT, 30% glass fibre FeaturesPBT for injection moulding, chemically reinforced with 30% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bending.. |