Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 6.69 GPa | 970 ksi | 1.3 mm/min; ASTM D790 |
PolyOne LubriOne™ PS-30GF/2S Natural Polybutylene Terephthalate (PBT) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
Flexural Modulus | 6.69 GPa @Temperature 23.0 °C |
970 ksi @Temperature 73.4 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® AT-1116 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AT-1116 HS polyphthalamide (PPA) is a toughened, heat stabilized 16% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stabi.. |
|||
Flexural Modulus | 6.69 GPa @Temperature 23.0 °C |
970 ksi @Temperature 73.4 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® AT-1116 HS Polyphthalamide (PPA), 16% Glass Fiber (Dry) Amodel® AT-1116 HS polyphthalamide (PPA) is a toughened, heat stabilized 16% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional s.. |
|||
Flexural Modulus | 6.69 GPa | 970 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP JF004 PES LNP THERMOCOMP* JF004 is a compound based on Polyethersulfone resin containing 20% Glass Fiber. |
|||
Flexural Modulus | 6.69 GPa | 970 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP JF004 PES (Asia Pacific) LNP* THERMOCOMP* JF004 is a compound based on Polyethersulfone resin containing Glass Fiber. |
|||
Flexural Modulus | 6.69 GPa | 970 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP JF004E PES (Asia Pacific) LNP* Thermocomp* JF004E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding. |
|||
Flexural Modulus | 6.69 GPa | 970 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP JF004EXP PES LNP* THERMOCOMP* JF004EXP is a compound based on Polyethersulfone resin containing 20% Glass Fiber. Added features of this material include: Easy Molding. |
|||
Flexural Modulus | 6.69 GPa | 970 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP JF004EXP PES (Asia Pacific) LNP* Thermocomp* JF004EXP is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding. |
|||
Flexural Modulus | 6.69 GPa | 970 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP JF004E PES LNP* THERMOCOMP* JF004E is a compound based on Polyethersulfone resin containing 20% Glass Fiber. Added features of this material include: Easy Molding. |