- Polymer Property : Flexural Modulus = 957 ksi
Polymer Property : Flexural Modulus = 957 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 6.60 GPa | 957 ksi | ISO 178 |
| PolyOne Bergadur™ PB400 G15 H UF UV Polybutylene Terephthalate (PBT) Information provided by PolyOne |
|||
| Flexural Modulus | 6.60 - 20.0 GPa | 957 - 2900 ksi | Average value: 11.5 GPa Grade Count:24 |
| Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max.. |
|||
| Flexural Modulus | 6.60 - 8.60 GPa | 957 - 1250 ksi | Average value: 7.50 GPa Grade Count:10 |
| Overview of materials for Phenolic, Resole, Wood Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Resole, Wood Filled". Each property range of values reported is minimum and maximum values of .. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | DIN 53 457 |
| Albis Plastics Tedur® L V 9112-2 PPS, 20% Glass Fiber
(discontinued **) Excellent Surface Finish (Additional Annealing May Be Necessary). Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Pipes, ProfilesProcessing: Extrusion (Melt Temperatur.. |
|||
| Flexural Modulus | 6.60 - 19.0985 GPa @Temperature -40.0 - 149 °C |
957 - 2770.04 ksi @Temperature -40.0 - 300 °F |
Average value: 10.3 GPa Grade Count:7 |
| Overview of materials for Nylon 66, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. .. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Kolon KOCETAL® CF702 Conductive Grade Acetal Resin Carbon fiber added, high stiffness and conductive grade. Applications: Conductive products. Information provided by API-Kolon. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-.. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-.. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 2mm/min; ISO 178 |
| Borealis GD310U Polypropylene Compound, Glass Fiber Reinforced GD310U is a 30% chemically coupled glass fiber reinforced polypropylene compound intended for injection molding. This material shows excellent mechanical properties also at elevated temperatures. .. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Plenco 2369 Phenolic, Granular, Injection Molded PLENCO 02369 is a general purpose, organic filled phenolic molding compound, formulated to minimize the generation of free ammonia for applications that are sensitive to such formation. PLENCO 02369.. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Tipco Tipcofil® AGM 602 - 10% Mineral & 20% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability 10% Mineral + 20% Glass Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | dry; ISO 178 |
| DSM Novamid® 1013GMF H2 NAT/BK37 PA6-GF30 30% Glass Reinforced, Heat Stabilized, Injection Molding, Excellent Dimensional Stability |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 2 mm/min; ISO 178 |
| Eurostar Starflam AF430B1 PA66, Glass Fiber Reinforced, Flame Retardant, Injection Molding Starflam AFR430B1 is a Flame Retardant, Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Adell BT-37 Nylon 6, 35% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Ashley Polymers Ashlene® 525-33G Nylon 66, 33% Glass Reinforced High impact Nylon 66 reinforced with 33% glass fibers, lubricated.Data provided by the manufacturer |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Ashley Polymers Ashlene® 990L-30G Nylon 610, 30% Glass Reinforced 30% glass reinforced for excellent dimensional stability and low water absorption.Data provided by the manufacturer |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Chem Polymer Chemlon 140 M Nylon 66, 40% Mineral Reinforced A 40% mineral reinforced nylon 66 exhibiting excellent stiffness in parts where control of warpage is essential.Data provided by the manufacturer, Chem Polymer. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Adell AJ-37 Nylon 66, 35% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Ashley Polymers Ashlene® 1430 Polycarbonate, 30% Glass Reinforced A 30% glass reinforced polycarbonate for increased mechanical strength and thermal properties. Also available with UV stabilizer. 1433: with UV stabilizer; 1433-H2: with improved UV stabilizer.Dat.. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Ashley Polymers Ashlene® 520-25G Nylon 66, 25% Glass Reinforced Nylon 66, 25% glass reinforced.Data provided by the manufacturer |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Ashley Polymers Ashlene® 61M Nylon 66, 40% Mineral reinforced A 40% mineral reinforced general purpose Nylon 66 resin with superior stiffness and dimensional stability.Data provided by the manufacturer |
|||
| Flexural Modulus | 6.60 - 35.0 GPa | 957 - 5080 ksi | Average value: 18.0 GPa Grade Count:54 |
| Overview of materials for Epoxy, Molded, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Molded, Glass Fiber Filler". Each property range of values reported is minimum and maximum values.. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| PolyOne Lubri-Tech™ MP-15MCF/15T-2S Modified PPO - 15% Milled Carbon Fiber - 15% PTFE - 2% Silicone
(disconti Data provided by PolyOne. |
|||