Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 2.97 GPa | 431 ksi | ASTM D790 |
PolyOne Geon™ HTX L1502 Polyvinyl Chloride Alloy (PVC Alloy) Physical properties based on Geon HTX L1502 white 1000.Information provided by PolyOne |
|||
Flexural Modulus | 2.97 GPa | 431 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP FARADEX NS0031 PC+ABS (Asia Pacific) Faradex NS0031 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel. Added features of this material include: EMI/RFI Shiel.. |
|||
Flexural Modulus | 2.97 GPa | 431 ksi | ISO 178 |
SABIC Innovative Plastics LNP Lubricomp RL0049 PA 66 LNP* Lubricomp* RL0049 is a compound based on Nylon 66 resin containing PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant.This data was supplied.. |
|||
Flexural Modulus | 2.97 GPa | 431 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RL0049S PA 66 LNP LUBRICOMP* RL0049S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Flame Retardant, Heat Stabilized, Wear Resistant. |
|||
Flexural Modulus | 2.97 GPa | 431 ksi | |
Shinil Chemical SHINSTRA PA-66 W100SRB Structural Polymer Abrasion Resistance SHINSTRA is the product line of structural polymer compound which exhibits excellent physical, mechanical, and thermal properties. Shinil uses the state-of-the-art dispersion and blending technolog.. |
|||
Flexural Modulus | 2.97 GPa | 431 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL EXNL0143 PPE+PS Noryl PX1736 Resin is a blend of PPE and PS, that provides high strength, increased heat resistance, and translucency. The material has melt strenght suitable for Extrusion and Blow Molding applica.. |
|||
Flexural Modulus | 2.97 GPa | 431 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL PX1736 PPE+PS Noryl PX1736 Resin is a blend of PPE and PS, that provides high strength, increased heat resistance, and translucency. The material has melt strenght suitable for Extrusion and Blow Molding applica.. |
|||
Flexural Modulus | 2.97 GPa @Temperature 120 °C |
431 ksi @Temperature 248 °F |
ASTM Test |
BASF Petra® 130 FR 30% Glass Filled PET Petra 130 FR is a 30% glass fiber reinforced, flame retardant injection molding polyethylene terephthalate feedstocks. It is recognized as UL 94V-0/5VA by Underwriters Laboratories. It is also avail.. |
|||
Flexural Modulus | 2.97 GPa @Temperature 120 °C |
431 ksi @Temperature 248 °F |
ASTM Test |
BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Conditioned) Ultramid 8333G HI is a 14% glass reinforced, impact modified PA6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a
balance of st.. |
|||
Flexural Modulus | 2.97 - 12.5 GPa @Temperature -40.0 - 121 °C |
431 - 1810 ksi @Temperature -40.0 - 250 °F |
Average value: 5.07 GPa Grade Count:10 |
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Flexural Modulus | 2.97 - 2.97 GPa @Temperature 120 - 120 °C |
431 - 431 ksi @Temperature 248 - 248 °F |
Average value: 2.97 GPa Grade Count:1 |
Overview of materials for Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant". Each property range of values re.. |