Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.0260 GPa | 3.77 ksi | ASTM D790 |
ExxonMobil Optema® TC-113 Ethylene Methyl Acrylate for Compounding
(discontinued **) Data provided by the manufacturer, Exxon Chemical.23.5% Methyl Acrylate. An Ethylene Methyl Acrylate copolymer which can be used as an impact modifier or compatibilizer in polymer compounds. It ca.. |
|||
Flexural Modulus | 0.0260 GPa | 3.77 ksi | 1% Secant, ASTM D790 |
ExxonMobil Escorene® LD-760 High EVA Compounding Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 27.5% vinyl acetate copolymer designed for specialty compounding applications. Excellent filler acceptance produces highly loaded concentrates.Ap.. |
|||
Flexural Modulus | 0.0260 - 12.4 GPa | 3.77 - 1800 ksi | Average value: 1.44 GPa Grade Count:725 |
Overview of materials for Polypropylene, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Molded". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Flexural Modulus | 0.0260 GPa | 3.77 ksi | 1.3 mm/min; ASTM D790 |
A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Flexural Modulus | 0.0260 GPa | 3.77 ksi | 1.3 mm/min; ASTM D790 |
A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Flexural Modulus | 0.0260 GPa | 3.77 ksi | 1.3 mm/min; ASTM D790 |
A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Flexural Modulus | 0.0260 GPa | 3.77 ksi | 1.3 mm/min; ASTM D790 |
A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Flexural Modulus | 0.0260 GPa | 3.77 ksi | 1.3 mm/min; ASTM D790 |
A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Flexural Modulus | 0.0260 GPa | 3.77 ksi | ASTM D790 |
DuPont Elvax® 360 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Flexural Modulus | 0.0260 GPa | 3.77 ksi | 1.3 mm/min; ASTM D790 |
A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |